Thermoplastic composite laminate and articles manufactured therefrom

1. A thermoplastic composite laminate comprising in order of:

(a) a top layer composed of at least one polycarbonate sheet;

(b) a fabric layer composed of a fabric comprising aromatic polyamide fibers and an adhesion aid; and

(c) a bottom layer composed of at least one polycarbonate sheet;

wherein

the top layer (a) is bound to the first surface of the fabric layer (b), and the bottom layer (c) is bound to the second surface of the fabric layer (b);

the aromatic polyamide fibers are produced from poly(p-phenylene terephthalamide) homopolymer, poly(p-phenylene terephthalamide) copolymer, poly(m-phenylene isophthalamide) homopolymer, poly(m-phenylene isophthalamide) copolymer, polysulfonamide homopolymer, polysulfonamide copolymer, or a mixture thereof;

the adhesion aid comprises polycarbonate oligomers have a weight average molecular weight of about 6500 or less; and

the thermoplastic composite laminate has an increase of about 30% or more in the shear strength as compared to that of a comparative laminate having the same fabric without the adhesion aid for the fabric layer (b), wherein the shear strength is measured according to the method of GB7124.

2. The thermoplastic composite laminate of claim 1 , wherein the total thickness of the thermoplastic composite laminate is from about 0.1 mm to about 10 mm.

3. The thermoplastic composite laminate of claim 1 , wherein the fabric for the fabric layer (b) contains the adhesion aid in an amount of from about 5 weight % to about 70 weight % of the adhesion aid, and the weight % is based on the total weight of the fabric.

4. The thermoplastic composite laminate of claim 1 , wherein the polycarbonate sheet for the top layer (a) and/or the bottom layer (c) comprises bisphenol A type polycarbonate polymers of general formula of 1:

where n is an integer of from about 50 to about 200.

5. The thermoplastic composite laminate of claim 4 , wherein the adhesion aid comprises polycarbonate oligomers of general formula of 2:

where m is an integer of from about 2 to about 25.

6. The thermoplastic composite laminate of claim 1 , wherein the fabric for the fabric layer (b) is produced by a method comprising:

i) applying a coating composition onto an untreated fabric to obtain a wet fabric;

ii) drying the wet fabric at a temperature ranging from ambient temperature to about 150° C. for from about 5 minute to about 180 minutes; and

iii) optionally, applying the coating composition onto the dried fabric of step ii) or rinsing the dried fabric of step ii), and drying by repeating step ii);

wherein

the step iii) is optionally repeated several times to obtain a treated fabric containing suitable amount of the adhesion aid;

the coating composition comprises an adhesion aid and a solvent;

the solvent is methanol, ethanol, 2-propanol, dichloromethane, chloroform, tetrahydrofuran, or mixtures thereof;

the adhesion aid comprises polycarbonate oligomers having an average molecular weight of about 6500 or less; and

the amount of the adhesion aid in the coating composition is from about 1 weight % to about 20 weight %, based on the total weight of the coating composition.

7. The thermoplastic composite laminate of claim 6 , wherein the method for applying the coating composition onto the untreated fabric is dipping, soaking, immersing, or spraying.

8. The thermoplastic composite laminate of claim 6 , wherein the areal density of the untreated fabric is from about 20 g/m 2 to about 660 g/m 2 .

9. The thermoplastic composite laminate of claim 1 is manufactured by a method selected from hot pressing, thermal compression molding, autoclave molding, and double-belt hot melt pressing.

10. An article comprising the thermoplastic composite laminate of claim 1 .

11. The article of claim 10 , which is housing or a protective cover for a mobile electronic device, a shell for a luggage, a decorative part for an auto control panel, or a face sheet for a snowboard.