Tapes

1. A tape which includes at least one layer comprising:

(a) endless fiber in a total amount of at least 40 volume % as compared to the total volume of the layer and

(b) a thermoplastic matrix comprising one or more polyamides containing one or more aliphatic monomeric units, and

(c) optionally at least one component selected from the group consisting of heat stabilizers, flame retardants, colorants, lubricants, mold release agents, UV stabilizers, impact modifiers, laser absorbing additives and combinations thereof; wherein

the one or more polyamides have a CH2-ratio of at least 5.5 and less than 10, calculated by the steps of:

(i) identifying the number of different aliphatic monomeric units in the one or more polyamides;

(ii) determining the number of CH2 groups per aliphatic monomeric unit for each of these different aliphatic monomeric units;

(iii) calculating the sum of the so determined numbers of CH2 groups; and

(iv) dividing said sum by the number of different aliphatic monomeric units in the one or more polyamides;

taking into account only the aliphatic monomeric units present in the one or more polyamides in an amount of at least 10 wt % with respect to the total weight of the one or more polyamides, wherein

the tape exhibits a high flexural modulus retention of 65.9% or more after 100 hours exposure to a solution of 30% H 2 SO 4 , wherein the flexural modulus is determined according to ISO 178.

2. The tape according to claim 1 , wherein the endless fiber is selected from the group consisting of glass fiber, carbon fiber, aramid fiber and combinations thereof.

3. The tape according to claim 1 , wherein the one or more polyamides is selected from the group consisting of PA-410, PA-510, PA-412, PA-512, PA-610, PA-612, PA-1010, as well as blends and copolyamides thereof.

4. The tape according to claim 1 , wherein the amount of endless fiber is between 40 and 65 volume % as compared to the total volume of the layer.

5. The tape according to claim 1 , wherein the tape consists of one layer.

6. The tape according to claim 1 , wherein the tape comprises an additional layer which does not comprise endless fiber, wherein the additional layer is formed of at least one material selected from the group consisting of EVOH, PA-6, PA-66, PA-410, PA-6T/6I and copolyamides thereof.

7. The tape according to claim 1 , wherein the tape has a thickness between 50 to 500 micron.

8. The tape according to claim 1 , wherein the tape has a width between 5 mm and 10.0 cm.

9. The tape according to claim 1 , wherein the polyamide is a homopolyamide selected from the group consisting of PA-410, PA-510, PA-412, PA512, PA-610 and PA-612.

10. The tape according to claim 1 , wherein the CH2 ratio is between 5.7 and 8.5.

11. The tape according to claim 1 , wherein the tape exhibits a high flexural modulus retention of 65.9% to 79.2% after 100 hours exposure to a solution of 30% H 2 SO 4 , wherein the flexural modulus is determined according to ISO 178.

12. A pressure vessel which comprises the tape according to claim 1 .

13. The pressure vessel according to claim 12 , wherein the pressure vessel exhibits a high burst pressure of at least 25 bar according to ECE R110.

14. The pressure vessel according to claim 12 , wherein the pressure vessel exhibits a high burst pressure of at least 300 bar according to ECE R110.

15. The pressure vessel according to claim 12 , wherein the pressure vessel exhibits a high burst pressure provides for high burst pressure of at least 1500 bar according to ECE R110.

16. A pipe, sheet material or local reinforcement which comprises the tape according to claim 1 .

17. A pressure vessel which comprises a hollow body formed of successive wraps of a consolidated tape material, wherein the tape material comprises:

(a) endless fiber in a total amount of at least 40 volume % as compared to the total volume of the layer and

(b) a thermoplastic matrix comprising at least one polyamide containing at least one aliphatic monomeric units, wherein the at least one polyamide has a CH2-ratio of at least 5.5 and less than 10 and is selected from the group consisting of PA-410, PA-610, PA-612, PA-1010 and blends and copolyamides thereof, and

(c) optionally at least one component selected from the group consisting of heat stabilizers, flame retardants, colorants, lubricants, mold release agents, UV stabilizers, impact modifiers, laser absorbing additives and combinations thereof; wherein

the pressure vessel has a burst pressure of at least 25 bar according to ECE R110.

18. The pressure vessel according to claim 17 , wherein the pressure vessel has a burst pressure of at least 300 bar according to ECE R110.

19. The pressure vessel according to claim 17 , wherein the pressure vessel has a burst pressure of at least 1500 bar according to ECE R110.

20. A process for preparing a vessel comprising the following steps:

(a) providing a support;

(b) providing a tape according to claim 1 ;

(c) wrapping the tape around the support while consolidating the tape by heat, thereby creating a hollow body; and

(d) cooling the hollow body to become solid.

21. The process according to claim 20 , wherein the support is a mandrel, and wherein the process further comprises removing the mandrel after step (d).

22. The process according to claim 20 , wherein before step (c) the process comprises wrapping an additional material around the support, wherein the additional material comprises EVOH, PA-6, PA-66, PA410, PA610, PA612, metal or combinations thereof.