High-manganese hot-dip aluminum-coated steel sheet having excellent coating adhesion
Provided is a high-manganese hot-dip aluminum-coated steel sheet comprising: a base steel sheet containing, by weight, 5% to 35% of Mn, 0.3 to 6% of Al, 0.1 to 1.2% of Si, the balanced amount of Fe, and inevitable impurities; a hot-dip aluminum-coated layer, formed on a surface of the base steel sheet, containing, by weight, 3 to 12% of Si and the balanced amount of Al, and inevitable impurities; and an alloy layer, 0.1 to 10 μm in thickness with a Fe—Al—Si—Mn-based alloy phase on an interface between the base steel sheet and the hot-dip aluminum-coated layer, containing, by weight, 40 to 70% of Al, 2 to 13% of Si, 3 to 9% of Mn, the balance amount of Fe, and inevitable impurities.
1. A high-manganese hot-dip aluminum-coated steel sheet comprising:
a base steel sheet including, by weight, 5 to 35% of Mn, 0.3 to 6% of Al, 0.1 to 1.2% of Si, and a balance of Fe and inevitable impurities;
a hot-dip aluminum-coated layer formed on a surface of the base steel sheet and including, by weight, 3 to 12% of Si, 0.1 to 10% of Mg, and a balance of Al and inevitable impurities; and
an alloy layer formed at an interface between the base steel sheet and the hot-dip aluminum-coated layer, the alloy layer consisting of, by weight, 40 to 70% of Al, 2 to 13% of Si, 3 to 9% of Mn, 1% or less of Mg, and a balance of Fe and inevitable impurities,
wherein the alloy layer has a thickness of 0.1 to 10 μm and includes an Fe—Al—Si—Mn-based alloy phase.
2. The high-manganese hot-dip aluminum-coated steel sheet of claim 1 , wherein the contents of Al and Si included in the base steel sheet satisfy Relational expression 1 below:
1.0≤[Al] b /[Si] b ≤10 [Relative expression 1]
where [Al] b and [Si] b denote contents (wt %) of Al and Si, respectively, included in the base steel sheet.
3. The high-manganese hot-dip aluminum-coated steel sheet of claim 1 , wherein the contents of Mn, Al, and Si included in the base steel sheet satisfy Relational expression 2 below:
5.0≤[Mn] b /([Al] b +[Si] b )≤12.0 [Relational expression 2]
where [Mn] b , [Al] b , and [Si] b denote contents (wt %) of Mn, Al, and Si, respectively, included in the base steel sheet.
4. The high-manganese hot-dip aluminum-coated steel sheet of claim 1 , wherein the base steel sheet further includes one or more selected from the group consisting of, by weight, 0.3 to 0.9% of C, 0.01 to 0.5% of Ti, 0.05 to 0.5% of V, 0.0005 to 0.0050% of B, 0.01 to 0.5% of Cr, 0.01 to 0.5% of Mo, 0.01 to 0.05% of Nb, and 0.01 to 0.1% of Sn.
5. The high-manganese hot-dip aluminum-coated steel sheet of claim 1 , wherein the hot-dip aluminum-coated layer further includes at least one selected from the group consisting of, by weight, 0.001 to 5 wt % of Ca, 0.005 to 2 wt % of Sr, 0.01 to 2 wt % of Mn, 0.01 to 2 wt % of Cr, 0.01 to 2 wt % of Mo, and 0.1 to 10 wt % of Sn.
6. The high-manganese hot-dip aluminum-coated steel sheet of claim 1 , wherein the thickness of the alloy layer is 3 to 7 μm.
7. The high-manganese hot-dip aluminum-coated steel sheet of claim 1 , wherein the thickness of the alloy layer satisfies Relational expression 3 below:
Ta≤(−0.78)×[ A ]+11.7
[ A ]=0.75[Si] p +0.15[Si] b +0.10[Al] b [Relational expression 3]
where T a denotes a thickness (μm) of the alloy layer, [Si] p denotes contents (wt %) of Si included in the hot-dip aluminum-coated layer, and [Si] b and [Al] b denote contents (wt %) of Si and Al, respectively, included in the base steel sheet.