Steel sheet for tool and manufacturing method therefor
The invention relates to a steel sheet for tool, and method for manufacturing thereof. An embodiment of the present invention is a steel sheet for a tool comprising 0.4 to 0.6 wt % of C, 0.05 to 0.5 wt % of Si, 0.1 to 1.5 wt % of Mn, 0.05 to 0.5 wt % of V, 0.1 to 2.0 wt % of at least of one or two components selected from the group comprising Ni, Cr, Mo, and combinations thereof, and the balance of Fe and inevitable impurities, with respect to 100 wt % of the total steel sheet, and provides a steel sheet for a tool of which the deviation of Rockwell hardness by the position in the width direction is within 5 HRC, and the ratio of those having a wave height in the longitudinal direction within 20 cm is 90% or more with respect to the wave height per 1 m of the steel sheet comprising the central portion in the longitudinal direction of the steel sheet for a tool.
1. A steel sheet for a tool comprising 0.4 to 0.6 wt % of C, 0.05 to 0.5 wt % of Si, 0.1 to 1.5 wt % of Mn, 0.05 to 0.5 wt % of V, at least one or two components selected from the group consisting of 0.05 to 1.0 wt % of Ni, 0.5 to 2.0 wt % of Cr, 0.5 to 2.0 wt % of Mo, and combinations thereof, and the balance of Fe and inevitable impurities, with respect to 100 wt % of the total steel sheet,
wherein the steel sheet consists of 70% or more of bainite structure, and the balance of ferrite and pearlite mixed structure with respect to 100% of a total microstructure of the steel sheet,
wherein the deviation of Rockwell hardness by the position in the width direction of the steel sheet for a tool is within 5 HRC,
wherein the ratio of those having a wave height in the longitudinal direction within 20 cm is 90% or more with respect to the wave height per 1 m of the steel sheet located in the central portion in the longitudinal direction of the steel sheet for a tool, and
wherein the Rockwell hardness of the steel sheet for a tool is 36 to 41 HRC.
2. The steel sheet for a tool of claim 1 , wherein the ratio of those having a wave height in the longitudinal direction within 10 cm is 90% or more with respect to the wave height per 1 m of the steel plate located in the central portion in the longitudinal direction of the steel sheet for a tool.
3. The steel sheet for a tool of claim 1 , wherein Mn: 0.1 to 1.0 wt %.
4. The steel sheet for a tool of claim 1 , wherein V: 0.05 to 0.3 wt %.
5. The steel sheet for a tool of claim 1 , wherein the steel sheet includes a total of 0.5 to 2.0 wt % of the at least one or two components selected from the group consisting of Ni, Cr, Mo, and combinations thereof.
6. The steel sheet for a tool of claim 1 , wherein the deviation of Rockwell hardness by the position in the width direction of the steel sheet for a tool is within 3 HRC.
7. The steel sheet for a tool of claim 1 , wherein a value of the combination of the thickness and the wave height of the steel sheet for a tool (wave height×thickness 2 ) is 2 cm 3 or less.
8. The steel sheet for a tool of claim 1 , wherein the thickness of the steel sheet for a tool is 5 mm or less.