Lead-free glass composition, glass composite material, glass paste, sealing structure, electrical/electronic component and coated component
The purpose of the present invention is to provide a lead-free glass composition in which crystallization is suppressed and which has a low softening point. This lead-free glass composition is characterized by containing silver oxide, tellurium oxide and vanadium oxide, and further containing at least one compound selected from among yttrium oxide, lanthanum oxide, cerium oxide, erbium oxide, ytterbium oxide, aluminum oxide, gallium oxide, indium oxide, iron oxide, tungsten oxide and molybdenum oxide as an additional component, and in that the content values (mol %) of silver oxide, tellurium oxide and vanadium oxide satisfy the relationships Ag 2 O>TeO 2 ≥V 2 O 5 and Ag 5 O≤2V 2 O 5 when calculated in terms of the oxides, and in that the content of TeO 2 is 25-37 mol. %.
1. A lead-free glass composition, containing silver oxide, tellurium oxide, and vanadium oxide,
further, as additional components, containing at least one of yttrium oxide, lanthanum oxide, cerium oxide, erbium oxide, ytterbium oxide, aluminum oxide, gallium oxide, indium oxide, and iron oxide,
wherein the contents (mol %) of the silver oxide, the tellurium oxide, and the vanadium oxide, when calculated in terms of the oxides as shown below, have the relationship of Ag 2 O>TeO 2 ≥V 2 O 5 , and Ag 2 O≤2V 2 O 5 , and
wherein the content of TeO 2 is 25 mol % to 37 mol %.
2. The lead-free glass composition according to claim 1 ,
wherein, when calculated in terms of the oxides, the content of Ag 2 O is equal to or greater than 40 mol % and less than 50 mol %, and the content of V 2 O 5 is equal to or greater than 20 mol % and less than 30 mol %.
3. The lead-free glass composition according to claim 1 ,
wherein the content of the additional component is, when calculated in terms of the oxides, 0.1 mol % to 3.5 mol %.
4. The lead-free glass composition according to claim 1 ,
wherein the additional component is at least one of yttrium oxide, lanthanum oxide, and aluminum oxide, and
wherein the content (mol %) of the additional component is, when calculated in terms of the oxides as shown below, Ag 2 O+Ln2O3≤2V 2 O 5 (Ln: Y, La, Al).
5. The lead-free glass composition according to claim 4 ,
wherein the content of the additional component is, when calculated in terms of the oxides, 0.3 mol % to 1.5 mol %.
6. The lead-free glass composition according to claim 1 ,
wherein the second endothermic peak temperature in differential thermal analysis is equal to or lower than 200° C.