Positive electrode for secondary battery, manufacturing method thereof, and lithium secondary battery including same

1. A method for manufacturing a positive electrode for a secondary battery, comprising:

applying a first positive electrode slurry including a first positive electrode active material on a positive electrode current collector;

in a first rolling step, rolling the first positive electrode slurry to form a first positive electrode mixture layeron the positive electrode current collector;

applying a second positive electrode slurry including a second positive electrode active material on the first positive electrode mixture layer; and

in a second rolling step, rollingthe second positive electrode slurry applied on the first positive electrode mixture layerto form a second positive electrode mixture layer, wherein the second positive electrode mixture layer is laminated with the first positive electrode mixture layer,

wherein the difference of elongation percentage of the first positive electrode mixture layer and the second positive electrode mixture layer is 0.2 to 0.7%.

2. The method of claim 1 , wherein the average particle diameter (D 50 ) of the first positive electrode active material is 5 to 80% of the average particle diameter (D 50 ) of the second positive electrode active material.

3. The method of claim 1 , wherein the average particle diameter (D 50 ) of the first positive electrode active material is 1 to 15 μm.

4. The method of claim 1 , wherein the average particle diameter (D 50 ) of the second positive electrode active material is 10 to 100 μm.

5. The method of claim 1 , wherein the elongation percentage of the first positive electrode mixture layer is 0.2 to 1.2%.

6. The method of claim 1 , wherein the elongation percentage of the second positive electrode mixture layer is 0.6 to 2.0%.

7. The method of claim 1 , wherein the total elongation percentage of a positive electrode including the first positive electrode mixture layer and the second positive electrode mixture layer is less than 1.4%.

8. The method of claim 1 , wherein at least one of the first positive electrode active material and the second positive electrode active material comprises a lithium transition metal oxide represented by Formula 1 below:

Li a Ni 1−x−y Co x Mn y M z O 2   [Formula 1]

(in which, M is any one or more elements selected from the group consisting of Al, Zr, Ti, Mg, Ta, Nb, Mo and Cr, and in which 0.9≤a≤1.5, 0≤x≤0.5, 0≤y≤0.5, 0≤z≤0.1, and 0≤x+y≤0.7.).

9. A positive electrode fora secondary battery, comprising:

a positive electrode current collector;

a first positive electrode mixture layer laminated on the positive electrode current collectorand including a first positive electrode active material;

a second positive electrode mixture layer laminated on the first positive electrode mixture layerand including a second positive electrode active material; and wherein

the difference of elongation percentage between the first positive electrode mixture layer and the second positive electrode mixture layer is 0.2 to 0.7%.

10. The positive electrode for a secondary battery of claim 9 , wherein the average particle diameter (D 50 ) of the first positive electrode active material is 5 to 80% of the average particle diameter (D 50 ) of the second positive electrode active material.

11. The positive electrode for a secondary battery of claim 9 , wherein the average particle diameter (D 50 ) of the first positive electrode active material is 1 to 15 μm.

12. The positive electrode for a secondary battery of claim 9 , wherein the average particle diameter (D 50 ) of the second positive electrode active material is 10 to 100 μm.

13. The positive electrode for a secondary battery of claim 9 , wherein the elongation percentage of the first positive electrode mixture layer is 0.2 to 1.2%, and wherein the elongation percentage of the second positive electrode mixture layer is 0.6 to 2.0%.

14. The positive electrode for a secondary battery of claim 9 , wherein the total elongation percentage of a positive electrode including the first positive electrode mixture layer and the second positive electrode mixture layer is less than 1.4%.

15. The positive electrode for a secondary battery of claim 9 , wherein the porosity of the first positive electrode mixture layer is 18 to 34%.

16. The positive electrode for a secondary battery of claim 9 , at least one of the first positive electrode active material and the second positive electrode active material comprises a lithium transition metal oxide represented by Formula 1 below:

Li a Ni 1−x−y Co x Mn y M z O 2   [Formula 1]

(in which, M is any one or more elements selected from the group consisting of Al, Zr, Ti, Mg, Ta, Nb, Mo and Cr, and in which 0.9≤a≤1.5, 0≤x≤0.5, 0≤y≤0.5, 0≤z≤0.1, and 0≤x+y≤0.7.).

17. A lithium second battery comprising:

an electrode assembly including a positive electrode, a negative electrode, and a separator interposed between the positive electrode and the negative electrode;

a battery case for housing the electrode assembly; and

a non-aqueous electrolyte injected into the battery case, wherein the positive electrode is a positive electrode according to claim 9 .

18. The method of claim 1 , wherein the difference of elongation percentage of the first positive electrode mixture layerand the second positive electrode mixture layeris 0.5 to 0.7%.

19. The positive electrode of claim 9 , wherein the difference of elongation percentage of the first positive electrode mixture layer and the second positive electrode mixture layer is 0.5 to 0.7%.