Lithium-containing composite oxide, cathode active material, positive electrode for lithium ion secondary battery, and lithium ion secondary battery
To provide a lithium-containing composite oxide, a cathode active material and a positive electrode for a lithium ion secondary battery, with which a lithium ion secondary battery having favorable cycle characteristics even when charged at a high voltage can be obtained; and a lithium ion secondary battery having favorable cycle characteristics even when charged at a high voltage. A lithium-containing composite oxide which is represented by Li a Ni b Co c Mn d M e O 2 wherein M is Mg, Ca, Al, Ti, V, Nb, Mo, W or Zr, a+b+c+d+e=2, “a” is from 1.01 to 1.10, b is from 0.30 to 0.95, c is from 0 to 0.35, d is from 0 to 0.35, and e is from 0 to 0.05, wherein in an X-ray diffraction pattern obtained by reflection X-ray diffraction employing Cu-Kα rays, the ratio (I 104 /I 110 ) of the integrated intensity (I 104 ) of a peak of (104) plane to the integrated intensity (I 110 ) of a peak of (110) plane is at least 4.20.
1. A lithium-containing composite oxide which is represented by the following formula (I):
Li a Ni b Co c Mn d M e O 2 formula (I)
wherein M is at least one member selected from the group consisting of Ca, Al, Ti, Nb, Mo, W and Zr, a+b+c+d+e=2, a is from 1.01 to 1.10, b is from 0.30 to 0.95, c is from 0 to 0.35, d is from 0 to 0.35, and 0<e≤0.05,
wherein in an X-ray diffraction pattern obtained by reflection X-ray diffraction employing Cu-Kα rays, the ratio (I 104 /I 110 ) of the integrated intensity (I 104 ) of a peak of (104) plane assigned to a crystal structure with space group R-3m to the integrated intensity (I 110 ) of a peak of (110) plane assigned to a crystal structure with space group R-3m is at least 4.20.
2. The lithium-containing composite oxide according to claim 1 , wherein with respect to the ratio (I 003 /I 104 ) of the integrated intensity (I 003 ) of a peak of (003) plane assigned to a crystal structure with space group R-3m to the integrated intensity (I 104 ) of a peak of (104) plane assigned to a crystal structure with space group R-3m in an X-ray diffraction pattern of the lithium-containing composite oxide, the value obtained by dividing the above ratio obtained by reflection X-ray diffraction employing Cu-Kα rays, by the above ratio obtained by transmission X-ray diffraction employing synchrotron radiation, is at least 1.18.
3. The lithium-containing composite oxide according to claim 1 , wherein with respect to the ratio (I 003 /I 104 ) of the integrated intensity (I 003 ) of a peak of (003) plane assigned to a crystal structure with space group R-3m to the integrated intensity (I 104 ) of a peak of (104) plane assigned to a crystal structure with space group R-3m in an X-ray diffraction pattern of the lithium-containing composite oxide, the value obtained by subtracting the above ratio obtained by transmission X-ray diffraction employing synchrotron radiation, from the above ratio obtained by reflection X-ray diffraction employing Cu-Kα rays, is at least 0.18.
4. The lithium-containing composite oxide according to claim 1 , wherein in the formula (I), a+b+c+d+e=2, a is from 1.01 to 1.10, b is from 0.40 to 0.55, c is from 0.15 to 0.35, d is from 0.20 to 0.35, and 0<e≤0.05.
5. The lithium-containing composite oxide according to claim 1 , wherein in an X-ray diffraction pattern of the lithium-containing composite oxide obtained by reflection X-ray diffraction employing Cu-Kα rays, the crystallite size obtained in accordance with the Scherrer equation from a peak of (110) plane assigned to a crystal structure with space group R-3m is from 30 to 70 nm.
6. A cathode active material containing the lithium-containing composite oxide as defined in claim 1 .
7. The cathode active material according to claim 6 , wherein D 50 of the cathode active material is from 3 to 15 μm.
8. A positive electrode for a lithium ion secondary battery, which comprises the cathode active material as defined in claim 6 , an electrically conductive material and a binder.
9. A lithium ion secondary battery, which comprises the positive electrode for a lithium ion secondary battery as defined in claim 8 , a negative electrode, a separator and a non-aqueous electrolyte.
10. A lithium-containing composite oxide which is represented by the following formula (I):
Li a Ni b Co c Mn d M e O 2 formula (I)
wherein M is at least one member selected from the group consisting of Ca, Al, Ti, Nb, Mo, W and Zr, a+b+c+d+e=2, a is from 1.01 to 1.10, b is from 0.30 to 0.95, c is from 0 to 0.35, d is from 0 to 0.35, and 0<e≤0.05,
wherein in an X-ray diffraction pattern obtained by reflection X-ray diffraction employing Cu-Kα rays, the ratio (I 104 /I 110 ) of the integrated intensity (I 104 ) of a peak of (104) plane assigned to a crystal structure with space group R-3m to the integrated intensity (I 110 ) of a peak of (110) plane assigned to a crystal structure with space group R-3m is at least 4.20 and at most 5.00.
11. The lithium-containing composite oxide according to claim 1 , wherein c is from 0.25 to 0.35.
12. A lithium-containing composite oxide which is represented by the following formula (I):
Li a Ni b Co c Mn d M e O 2 formula (I)
wherein M is at least one member selected from the group consisting of Ca, Al, Ti, Nb, Mo, and Zr, a+b+c+d+e=2, a is from 1.01 to 1.10, b is from 0.30 to 0.95, c is from 0 to 0.35, d is from 0 to 0.35, and 0<e≤0.05,
wherein in an X-ray diffraction pattern obtained by reflection X-ray diffraction employing Cu-Kα rays, the ratio (I 104 /I 110 ) of the integrated intensity (I 104 ) of a peak of (104) plane assigned to a crystal structure with space group R-3m to the integrated intensity (I 110 ) of a peak of (110) plane assigned to a crystal structure with space group R-3m is at least 4.20.