Cathode active material, positive electrode for lithium ion secondary battery, and lithium ion secondary battery
To provide a cathode active material with which it is possible to obtain a lithium ion secondary battery having a high discharge capacity and being excellent in the cycle characteristic even after 50 cycles; a positive electrode using it; and a lithium ion secondary battery. A cathode active material, which comprises a lithium-containing composite oxide represented by the formula: aLi(L 1/3 Mn 2/3 )O 2 .(1−a)LiMO 2 wherein M is at least one transition metal element selected from Ni, Co and Mn, and 0<a<1; wherein when the lithium-containing composite oxide is electrochemically oxidized to a potential of 4.5 V vs. Li/Li + , in an X-ray diffraction pattern, the integral breadth of a peak of (003) plane assigned to a crystal structure with space group R-3m is at most 0.38 deg, and the integral breadth of a peak of (104) plane assigned to a crystal structure with space group R-3m is at most 0.54 deg.
1. A cathode active material contained in a positive electrode of a lithium ion secondary battery, which comprises a lithium-containing composite oxide represented by the following formula (1):
a Li(Li 1/3 Mn 2/3 )O 2 .(1− a )LiMO 2 formula (1)
wherein M is at least one transition metal element selected from Ni, Co and Mn, and “a” is higher than 0 and less than 1;
wherein the lithium-containing composite oxide contained in the lithium ion secondary battery charged to a potential of 4.5 V vs. Li/Li + is such that, in an X-ray diffraction pattern, the integral breadth of a peak of (003) plane assigned to a crystal structure with space group R-3m is at most 0.38 deg, and the integral breadth of a peak of (104) plane assigned to a crystal structure with space group R-3m is at most 0.54 deg, and
wherein the specific surface area of the cathode active material is from 0.5 to 5 m 2 /g.
2. The cathode active material according to claim 1 , the lithium-containing composite oxide contained in the lithium ion secondary battery charged to a potential of 4.5 V vs. Li/Li + is such that, in an X-ray diffraction pattern, the ratio (H 018 /H 110 ) of the height (H 018 ) of a peak of (018) plane assigned to a crystal structure with space group R-3m to the height (H 110 ) of a peak of (110) plane assigned to a crystal structure with space group R-3m is at least 0.27.
3. The cathode active material according to claim 1 , wherein of the lithium-containing composite oxide, in an X-ray diffraction pattern, the ratio (I 003 /I 104 ) of the integrated intensity (I 003 ) of a peak of (003) plane assigned to a crystal structure with space group R-3m to the integrated intensity (I 104 ) of a peak of (104) plane assigned to a crystal structure with space group R-3m is from 1.015 to 1.5.
4. The cathode active material according to claim 1 , wherein the lithium-containing composite oxide contained in the lithium ion secondary battery charged to a potential of 4.5 V vs. Li/Li + is such that in an X-ray diffraction pattern of the lithium-containing composite oxide, the ratio (H 020 /H 003 ) of the height (H 020 ) of a peak of (020) plane assigned to a crystal structure with space group C2/m to the height (H 003 ) of a peak of (003) plane assigned to a crystal structure with space group R-3m is at least 0.01.
5. The cathode active material according to claim 1 , wherein of the lithium-containing composite oxide, to the total molar amount (X) of Ni, Co and Mn, the ratio (Ni/X) of the molar amount of Ni is from 0.15 to 0.5, the ratio (Co/X) of the molar amount of Co is from 0 to 0.2, and the ratio (Mn/X) of the molar amount of Mn is from 0.45 to 0.8.
6. The cathode active material according to claim 1 , wherein D 50 of the cathode active material is from 3 to 15 μm.
7. The cathode active material according to claim 1 , wherein in an X-ray diffraction pattern of the lithium-containing composite oxide, the crystallite size obtained by the Scherrer equation from a peak of (003) plane assigned to a crystal structure with space group R-3m is from 60 to 140 nm.
8. The cathode active material according to claim 1 , wherein in an X-ray diffraction pattern of the lithium-containing composite oxide, the crystallite size obtained by the Scherrer equation from a peak of (110) plane assigned to a crystal structure with space group R-3m is from 30 to 90 nm.
9. A positive electrode for a lithium ion secondary battery, which comprises a cathode active material layer containing the cathode active material as defined in claim 1 , an electrically conductive material and a binder, on a positive electrode current collector.
10. A lithium ion secondary battery, which comprises the positive electrode for a lithium ion secondary battery as defined in claim 9 , a negative electrode, a separator and a non-aqueous electrolyte.
11. A cathode active material contained in a positive electrode of a lithium ion secondary battery, which comprises a lithium-containing composite oxide represented by the following formula (2):
a Li(Li 1/3 Mn 2/3 )O 2 .(1− a )LiNi α Co β Mn γ O 2 formula (2)
wherein “a” is higher than 0 and less than 1, “α” is higher than 0 and less than 1, “β” ranges from 0 to less than 1, and “γ” is higher than 0 and less than 1;
wherein the lithium-containing composite oxide is electrochemically oxidized to a potential of 4.5 V vs. Li/Li + ; in an X-ray diffraction pattern, the integral breadth of a peak of (003) plane assigned to a crystal structure with space group R-3m is at most 0.38 deg, and the integral breadth of a peak of (104) plane assigned to a crystal structure with space group R-3m is at most 0.54 deg.