Method for manufacturing panel-like formed article

1. A method for manufacturing a panel article having a polygonal top sheet portion, standing wall portions extending from, out of sides of the top sheet portion, at least two adjacent sides, and a level difference portion provided in each of the standing wall portions constituting at least one set of adjacent standing wall portions, the method comprising:

preparing a blank material made of a metal sheet having a tensile strength of 390 MPa or more and 980 MPa or less; and

press-forming the blank material in a cold manner to form the blank material into the panel article,

wherein, in the press-forming,

by using a pressing apparatus having a die which has a contour-carving portion in which a shape of the panel article is formed,

a first punch which faces the die and has a front end surface in which a shape of the top sheet portion is formed,

a second punch which is adjacent to an outside of the first punch, faces the die, and has a front end surface in which a shape of the level difference portion is formed, and

a blank holder which is adjacent to at least a part of an outside of the second punch and faces the die, wherein the first punch and the second punch are individually movable with respect to the die and the blank holder,

the blank material is disposed between the die and the blank holder, the first punch, and the second punch, the blank holder, the first punch, and the second punch are relatively moved with respect to the die, thereby pressing the first punch and the second punch to the blank material, and

pressing of the second punch to the blank material is completed earlier than pressing of the first punch to the blank material.

2. The method for manufacturing the panel article according to claim 1 ,

wherein, in the press-forming, the pressing of the first punch to the blank material begins when or after the pressing of the second punch to the blank material is completed.

3. The method for manufacturing the panel article according to claim 1 ,

wherein, in the press-forming, the pressing of the first punch to the blank material begins before the pressing of the second punch to the blank material is completed.

4. The method for manufacturing the panel article according to claim 1 ,

wherein, when a depth from a criterion surface facing the blank holder to a level difference surface facing the second punch is represented by d 1 (mm), and a depth from the criterion surface to a contour bottom surface facing the first punch is represented by d 2 (mm), the contour-carving portion of the die of the pressing apparatus satisfies d 2 ≥40 and d 1 /d 2 <0.8.

5. The method for manufacturing the panel article according to claim 1 ,

wherein the blank material is a steel sheet.

6. The method for manufacturing the panel article according to claim 5 ,

wherein the steel sheet is a tailored blank.

7. The method for manufacturing the panel article according to claim 1 ,

wherein the blank material has an opening portion at a location corresponding to the top sheet portion.

8. The method for manufacturing the panel article according to claim 2 ,

wherein, when a depth from a criterion surface facing the blank holder to a level difference surface facing the second punch is represented by d 1 (mm), and a depth from the criterion surface to a contour bottom surface facing the first punch is represented by d 2 (mm), the contour-carving portion of the die of the pressing apparatus satisfies d 2 ≥40 and d 1 /d 2 <0.8.

9. The method for manufacturing the panel article according to claim 3 ,

wherein, when a depth from a criterion surface facing the blank holder to a level difference surface facing the second punch is represented by d 1 (mm), and a depth from the criterion surface to a contour bottom surface facing the first punch is represented by d 2 (mm), the contour-carving portion of the die of the pressing apparatus satisfies d 2 ≥40 and d 1 /d 2 <0.8.