A production method includes a placement step, a first pressing step, and a second pressing step. In the placement step, a blank plate is placed in press tooling. In the first pressing step, the blank plate is caused to undergo bend forming in such a way that concave ridges, a concave area, and areas of concave-correspondence vertical wall areas that are areas adjacent to the concave ridges are formed in the blank plate. In the second pressing step, the resultant plate is caused to undergo draw forming in such a way that convex ridges, a convex area, areas of convex-correspondence vertical wall areas that are areas adjacent to the convex ridges are formed in the resultant plate.
1. A method for producing an intermediate formed product, the intermediate formed product to be further processed into a press-formed product,
the production method comprising:
placing a blank metal plate in such a way that the blank metal plate extends off opposite sides of a vertex of a first punch;
causing the blank plate to undergo bend forming by using the first punch, a pad, and a first die in such a way that concave ridges, a concave area, and areas of concave-correspondence vertical wall areas that are areas adjacent to the concave ridges are formed in the blank plate to produce an initial intermediate formed product; and
causing the initial intermediate formed product to undergo draw forming by using a second punch, a second die, and a blank holder in such a way that convex ridges, a convex area, areas of convex-correspondence vertical wall areas that are areas adjacent to the convex ridges, and second ridges located opposite the concave and convex ridges are formed in the initial intermediate formed product to form the intermediate formed product, the second ridges being part of vertical wall sections having the concave-correspondence vertical wall areas adjacent to the concave ridges and the convex-correspondence vertical wall areas adjacent to the convex ridges.
2. A method for producing a press-formed product comprising:
providing an intermediate formed metal product, the intermediate formed metal product comprising:
concave ridges, a concave area, and areas of concave-correspondence vertical wall areas that are areas adjacent to the concave ridges; and
convex ridges, a convex area, areas of convex-correspondence vertical wall areas that are areas adjacent to the convex ridges, and
additional ridges located opposite the concave and convex ridges, the additional ridges being part of vertical wall sections having the concave-correspondence vertical wall areas adjacent to the concave ridges and the convex-correspondence vertical wall areas adjacent to the convex ridges, and
a top plate section between the convex ridges and concave ridges, and
performing bend forming on the intermediate formed metal product, the bend forming moving the additional ridges of the vertical wall sections toward an outer side of the vertical wall sections to form the press-formed product, the press-formed product including:
the top plate section located between the convex ridges and concave ridges,
the vertical wall sections extending from the top plate section via the convex ridges and concave ridges,
each of the concave ridges convexly curved toward an inner side of the corresponding vertical wall section and each of the convex ridges convexly curved toward the outer side of the corresponding vertical wall section,
a linear distance between a center of each of the concave ridges and a center of the corresponding convex ridge being 15 times a spacing between the convex ridges and concave ridges or less,
the top plate section having the concave area located between the concave ridges and the convex area located between the convex ridges,
the vertical wall sections having the concave-correspondence vertical wall areas adjacent to the concave ridges and the convex-correspondence vertical wall areas adjacent to the convex ridges, the additional ridges located in positions opposite the convex ridges and concave ridges.
3. The method for producing an intermediate formed product according to claim 1 ,
wherein the blank plate is a steel plate, and yield strength of the blank plate is 400 MPa or more.
4. The method for producing an intermediate formed product according to claim 1 ,
wherein the blank plate is a steel plate, and yield strength of the blank plate is 600 MPa or more.
5. The method for producing an intermediate formed product according to claim 1 ,
wherein a plate thickness of the blank plate ranges from 0.8 to 1.6 mm.
6. The method for producing an intermediate formed product according to claim 1 ,
wherein a following Formula (6) is satisfied:
0.011< t/W< 0.032 (6)
where symbols in the Formula mean as follows:
t [mm] represents a plate thickness of the blank plate;
W [mm] represents a spacing between the two ridges.