Material, storage container using the material, valve attached to the storage container, method of storing ClF and method of using ClF storage container
A material at least partly coated with a passive film of fluoride formed by contact with a gas containing ClF.
1. A storage container
characterized in that the storage container is made of a material, the material is at least partly coated with a passive film of fluoride formed by contact with a gas containing ClF;
characterized in that the storage container has an inner surface coated with the passive film; and
characterized in that the storage container has a valve attached thereto, the valve having
a flow passage for the gas to flow through,
a valve seat through which the flow passage passes, and
a valve member brought into contact with or away from the valve seat to close or open the flow passage, wherein
the flow passage and the portions of the valve seat and valve member which are to be exposed to a gas are coated with the passive film.
2. The storage container according to claim 1 , characterized in that
the valve member has a sealing surface pressed against the valve seat to close the flow passage, and
the sealing surface has a gold plating layer with a thickness of 2 μm to 10 μm.
3. The storage container according to claim 2 , characterized in that the gold plating layer is sealed.
4. The storage container according to claim 2 , characterized in that the gold plating layer is oxidatively treated.
5. The storage container according to claim 2 , characterized in that the gold plating layer is coated with the passive film.
6. The storage container according to claim 1 , characterized in that the valve member is a disc shape.
7. The storage container according to claim 2 , characterized in that the valve member is a diaphragm.
8. The material according to claim 1 , characterized in that the passive film has a thickness of 5 nm to 50 nm.
9. The material according to claim 1 , characterized in that the gas further contains one or more substances chosen from a group consisting of ClF 3 and F 2 .
10. The material according to claim 1 , characterized in that the material comprises at least one of substances: manganese steel, stainless steel, chrome molybdenum steel, nickel alloy, aluminum alloy, cobalt alloy, gold and resin, and is coated with the passive film.