Method of making a dental restoration
A method of making a monolithic dental restoration. The method includes the steps of providing a monolithic precursor of a dental restoration and firing the monolithic dental restoration precursor to provide the monolithic dental restoration. The zirconia material of both the dental restoration precursor as well as the dental restoration has a relative density of greater than 98% of the theoretic density of the zirconia material. The invention helps providing a color of a non-glazed dental restoration which resembles the color of a glazed dental restoration.
1. A method of making a monolithic dental restoration, comprising:
providing a green body monolithic precursor of a dental restoration;
sintering the green body to provide a monolithic precursor of a dental restoration being made of zirconia material having a relative density of greater than 98% of the theoretic density of the zirconia material;
polishing the monolithic dental restoration precursor; and
firing the monolithic dental restoration precursor at a temperature of at least 800° C. for a duration of at least 10 seconds to provide the monolithic dental restoration, wherein the monolithic dental restoration precursor does not have a glazing;
wherein the firing step comprises a heating phase, a steady state phase, and a cooling phase, and wherein the steady state phase is performed for a duration of less than 10 minutes, wherein the duration of the firing refers to the duration of the steady state phase.
2. The method of claim 1 , wherein zirconia material comprising between 85% by weight and 95% by weight ZrO 2 .
3. The method of claim 1 wherein the green body is made of zirconia material having a relative density which is between about 40% and about 70% of the theoretic density of the zirconia material.
4. The method of claim 3 , further comprising providing the green body by milling or grinding from a blank of zirconia material.
5. The method of claim 3 , further comprising soaking the green body with a coloring liquid.
6. The method of claim 5 , further comprising drying the green body soaked with the coloring liquid.
7. The method of claim 3 , further comprising smoothing the green body.
8. The method of claim 1 , comprising providing the monolithic dental restoration precursor in a pre-colored form.
9. The method of claim 1 , wherein the step of sintering causes the relative density to be increased to the relative density of greater than 98%.
10. The method claim 1 , wherein the step of polishing the monolithic dental restoration precursor comprises applying a polishing paste on the monolithic dental restoration precursor and polishing the monolithic dental restoration precursor by use of the polishing paste and a polishing tool.
11. The method of claim 8 , wherein the pre-colored dental restoration precursor is made of a zirconia material comprising between about 5% by weight to 10% by weight yttrium oxide, Er 2 O 3 , Tb 4 O 7 , Bi 2 O 3 , MnO, and Fe 2 O 3 ; and wherein Er 2 O 3 is present in an amount up to about 1% by weight, Tb 4 O 7 is present in an amount up to about 1% by weight, Bi 2 O 3 is present in an amount up to about 0.3% by weight, MnO is present in an amount up to about 0.05%, and Fe 2 O 3 is present in an amount up to about 0.5% by weight.