Visbreaking process
View Patent ↗A process for increasing MFR 2 of a polyethylene copolymer or an ethylene plastomer or elastomer comprising: (I) extruding a copolymer of polyethylene copolymer having a density of 910 to 970 kg/m 3 and an MFR 2 of 1 and 100 g/10 min or an ethylene plastomer or elastomer having a density of 855 to 910 kg/m 3 and an MFR 2 of 0.5 and 100 g/10 min in the presence of 0.1 to 2 wt % of a non-peroxide radical initiator so as to produce a polyethylene copolymer having an MFR 2 of 200 g/10 min or more, or an ethylene plastomer or elastomer having a MFR 2 of 200 g/10 min or more.
1. A process for increasing the MFR 2 of a polyethylene copolymer or an ethylene plastomer or elastomer, the process comprising:
extruding a copolymer of polyethylene having a density of from 910 to 970 kg/m 3 and an MFR 2 of from 1 to 100 g/10 min in the presence of from 0.1 to 2 wt % of a radical initiator so as to produce a polyethylene copolymer having an MFR 2 of 200 g/10 min or more, or
extruding an ethylene plastomer or elastomer having a density of from 855 to 910 kg/m 3 and an MFR 2 of from 0.5 to 100 g/10 min in the presence of 0.1 to 2 wt % of a radical initiator so as to produce an ethylene plastomer or elastomer having an MFR 2 of 200 g/10 min or more,
wherein the radical initiator comprises a non-peroxide radical initiator, a radical initiator which decomposes at a temperature greater than 200° C., or a combination thereof.
2. The process of claim 1 , wherein the radical initiator decomposes at a temperature greater than 200° C.
3. The process of claim 1 , wherein the extruding is performed by an extruder operated with a screw speed of from 300 to 1400 rpm.
4. The process of claim 1 , wherein the produced polyethylene copolymer or ethylene plastomer or elastomer has an MFR 2 which is 200 g/10 min or more higher than the MFR 2 before extrusion.
5. The process of claim 1 , wherein the MFR 2 of the polyethylene copolymer or ethylene plastomer or elastomer after extrusion is at least 500 g/10 min.
6. The process of claim 1 , wherein the MFR 2 of the polyethylene copolymer or ethylene plastomer or elastomer before extrusion is from 1 to 10 g/10 min.
7. The process of claim 1 , wherein the extruding is performed by an extruder comprising a barrel, wherein heat is applied to the barrel at a maximum temperature of at least 300° C.
8. The process of claim 3 , wherein the screw speed in the extruder is from 300 to 1200 rpm.
9. The process of claim 3 , wherein the extruder provides a specific energy input (SEI) of 0.15 kWh/kg or more.
10. The process of claim 1 , wherein all of the radical initiator is added at the start of the extrusion.
11. A method comprising using extruder screw speed or radical initiator content to control the MFR 2 of a visbroken polyethylene copolymer or ethylene plastomer or elastomer in a process in which:
a polyethylene copolymer having a density of from 910 to 970 kg/m 3 and an MFR 2 of from 1 to 100 g/10 min, or
an ethylene plastomer or elastomer having a density of from 855 to 910 kg/m 3 and an MFR 2 of from 0.5 to 100 g/10 min
is extruded in the presence of from 0.1 to 2 wt % of a radical initiator so as to produce: a polyethylene copolymer having an MFR 2 of 200 g/10 min or more, or an ethylene plastomer or elastomer having a MFR 2 of 200 g/10 min or more.