Clean aluminum alloys
A method comprises providing a molten aluminum alloy selected from the group consisting of 6000 series aluminum alloys. The molten aluminum alloy is formed into a formed body having beta-AlFeSi particles. The formed body is solution heat treated at a temperature in a range of 1,025-1,070° F. to form a heat treated body. The solution heat treating transforms substantially all of the beta-AlFeSi particles into alpha-AlFeSi particles such that the heat treated body is substantially free of the beta-AlFeSi particles.
1. A cast aluminum alloy article formed from a 6000 series aluminum alloy comprising less than 0.04 wt % Fe, the 6000 series aluminum alloy further comprising AlFeSi particles, wherein the cast aluminum alloy article is solution heat treated at a temperature in a range of 1,025-1,050° F. such that greater than 95% AlFeSi particles comprise alpha-AlFeSi particles and less than 5% AlFeSi particles comprise beta-AlFeSi particles, and further comprising a substantially continuous anodized layer of aluminum oxide covering an exterior surface of the cast aluminum alloy artice wherein the cast aluminum alloy article has a breakdown voltage of greater than 1,180 V/mil.
2. The cast aluminum alloy article of claim 1 , wherein greater than 99% of the AlFeSi particles comprise alpha-AlFeSi particles such that the article is substantially free of beta-AlFeSi particles.
3. The cast aluminum alloy article of claim 1 , comprising greater than 98 wt % Al.
4. The cast aluminum alloy article of claim 1 , comprising about 0.5-0.6 wt % Si, 0.16-0.19 wt % Cu, 0.05-0.065 wt % Cr and 1.0-1.1 wt % Mg.
5. The cast aluminum alloy article of claim 3 , comprising 0.1-0.15 wt % Sr.
6. The cast aluminum alloy article of claim 1 , wherein the aluminum alloy comprises a 6061 aluminum alloy.
7. The cast aluminum alloy article of claim 1 , having a % elongation in a range of 5-15%, a yield strength in a range of 42-44 KSI and an ultimate tensile strength in a range of 44-46 KSI.
8. The cast aluminum alloy article of claim 1 , wherein the alloy is covered with a substantially continuous anodized layer of aluminum oxide.
9. A cast aluminum alloy article formed from a 6000 series aluminum alloy comprising less than 0.04 wt % Fe, the 6000 series aluminum alloy further having AlFeSi particles, wherein the cast aluminum alloy article is solution heat treated at a temperature in a range of 1,025-1,050° F. such that the AlFeSi particles comprise alpha-AlFeSi particles having an average size in a range of 9-20 microns and an average spacing in a range of 100-250 microns, and further comprising a substantially continuous anodized layer of aluminum oxide on an exterior of the cast aluminum alloy article wherein the cast aluminum alloy article has a breakdown voltage of greater than 1,180 V/mil.
10. The cast aluminum alloy article of claim 9 , wherein greater than 95% of the AlFeSi particles comprise alpha-AlFeSi particles and less than 1% of the AlFeSi particles comprise beta-AlFeSi particles.
11. The cast aluminum alloy article of claim 10 , wherein greater than about 99% of the AlFeSi particles comprise alpha-AlFeSi particles such that the article is substantially free of beta-AlFeSi particles.
12. The cast aluminum alloy article of claim 9 , comprising greater than 98 wt % Al.
13. The cast aluminum alloy article of claim 9 , comprising about 0.5-0.6 wt % Si, 0.16-0.19 wt % Cu, 0.05-0.065 wt % Cr and 1.0-1.1 wt % Mg.
14. The cast aluminum alloy article of claim 12 , comprising 0.1-0.15 wt % Sr.
15. The cast aluminum alloy article of claim 9 , wherein the aluminum alloy comprises a 6061 aluminum alloy.
16. The cast aluminum alloy article of claim 9 , having a percent elongation in a range of 5-15%, a yield strength in a range of 42-44 KSI and an ultimate tensile strength in a range of 44-46 KSI.
17. The cast aluminum alloy article of claim 1 , wherein the cast aluminum alloy article has an admittance of less than 6 μMhos.
18. The cast aluminum alloy article of claim 1 , wherein the cast aluminum alloy article has a corrosion resistance of equal to or greater than 9 hours in 5 wt % HCl.
19. The cast aluminum alloy article of claim 9 , wherein the cast aluminum alloy article has an admittance of less than 6 μMhos.
20. The cast aluminum alloy article of claim 9 , wherein the cast aluminum alloy article has a corrosion resistance of equal to or greater than 9 hours in 5 wt % HCl.