Imageable polymers
This invention relates to imageable polymers, particularly those comprising poly vinylalcohol and to methods for making them as well as to embolic microspheres comprising the polymers. The microspheres are imageable during embolization procedures and can be loaded with drugs or other therapeutic agents to provide an imageable drug delivery system.
1. Hydrogel polymer microspheres wherein the hydrogel polymer comprises: a polyvinyl alcohol (PVA) backbone comprising at least two pendant chains having cross-linkable ethylenically unsaturated functional groups which are cross linked by a vinylic co-monomer;
wherein the PVA comprising 1,3 diol groups is acetalised with a radiopaque species which is coupled to the hydrogel polymer through a cyclic acetal group, the radiopaque species comprising one or more covalently bound iodines.
2. Hydrogel polymer microspheres according to claim 1 wherein the pendant chains comprising cross-linkable ethylenically unsaturated functional groups are attached to the 1,3 diol groups of the PVA backbone via cyclic acetal linkages.
3. Hydrogel polymer microspheres according to claim 1 wherein the vinylic co-monomer is 2-acrylamido-2-methylpropanesulfonic acid.
4. Hydrogel polymer microspheres according to claim 1 wherein the ethylenically unsaturated functional groups are acrylate groups.
5. Hydrogel polymer microspheres according to claim 1 wherein the radiopaque species comprises an iodinated phenyl group.
6. Hydrogel polymer microspheres according claim 1 wherein the radiopaque species is coupled to the hydrogel polymer through a cyclic acetal group, such that the hydrogel polymer comprises a structure according to the general formula I:
wherein X is a group of the formula:
wherein
Z is a linking group bonded to the cyclic acetal, or is absent, such that the phenyl group is bonded to the cyclic acetal; if Z is present, then Z is C 1-6 alkylene, or C 1-6 alkoxyalkylene;
Hal is 1,2,3 or 4 covalently attached iodines.
7. Hydrogel polymer microspheres according to claim 6 wherein, Z is (i) a methylene or ethylene group or is (ii) a group —(CH 2 ) p —O—(CH 2 ) q — wherein q is 0, 1 or 2 and p is 1 or 2 or is (iii) absent.
8. Hydrogel polymer microspheres according to claim 6 wherein, Z is —CH 2 O—, —(CH 2 ) 2 O—, —CH 2 OCH 2 —, —(CH 2 ) 2 O(CH 2 ) 2 — or is absent.
9. Hydrogel polymer microspheres according to claim 6 wherein Hal is 3 or 4 iodines.
10. Hydrogel polymer microspheres according to claim 6 wherein Hal is 2,3,5 triiodo, 2,4,6 triiodo or 2,3,4,6 tetraiodo.
11. Hydrogel polymer microspheres according to claim 1 wherein the radiopaque species is coupled to the hydrogel polymer through a cyclic acetal group, such that the hydrogel polymer comprises a structure according to any of the general formulas Ia to Ie
12. Hydrogel polymer microspheres according to claim 1 wherein the hydrogel polymer has a net charge at pH 7.4.
13. Hydrogel polymer microspheres according to claim 12 wherein the hydrogel polymer has a net negative charge at pH 7.4.
14. Hydrogel polymer microspheres according to claim 1 having a mean diameter size range of from 10 to 2000 μm.
15. A composition comprising hydrogel polymer microspheres according to claim 1 and a therapeutic agent wherein the therapeutic agent is electrostatically held within the hydrogel matrix.
16. The composition according to claim 15 wherein the therapeutic agent is selected from the group consisting of camptothecins, anthracyclines, antiangiogenic agents, microtubule assembly inhibitors, aromatase inhibitors, platinum drugs and nucleoside analogues.
17. The composition according to claim 16 wherein the therapeutic agent is selected from the group consisting of irinotecan, topotecan, doxorubicin, daunorubicin, idarubicin, epirubicin, axitinib, bortezomib, bosutinib canertinib, dovitinib, dasatinib, erlotinib gefitinib, imatinib, lapatinib, lestaurtinib, masutinib, mubitinib, pazopanib, pazopanib semaxanib, sorafenib, sunitinib tandutinib, vandetanib, vatalanib vismodegib, vinblastine, vinorelbine, vincristine, anastrazole, cisplatin oxaliplatin carboplatin, miriplatin, 5-FU, cytarabine, fludarabine, gemcitabine paclitaxel, docetaxel, mitomycin, mitoxantrone, bleomycin, pingyangmycin, abiraterone, amifostine, buserelin, degarelix, folinic acid, goserelin, lanreotide, lenalidomide, letrozole, leuprorelin, octreotide, tamoxifen, triptorelin, bendamustine, chlorambucil, dacarbazine, melphalan, procarbazine, temozolomide, rapamycin, zotarolimus, everolimus, umirolimus, sirolimus, methotrexate, pemetrexed and raltitrexed.
18. A method of making hydrogel microspheres according to claim 1 comprising the steps of:
(a) swelling the hydrogel microspheres in a solvent capable of swelling the hydrogel polymer; and
(b) contacting the swollen hydrogel microspheres with a solution of the radiopaque species capable of forming a cyclic acetal with a 1,3 diol under acidic conditions; and
(c) extracting the hydrogel microspheres.
19. The method according to claim 18 , further comprising the step of drying the extracted microspheres.
20. The method according to claim 18 , wherein the solvent is a polar organic solvent.
21. The method according to 18 , wherein step (b) is conducted at a temperature greater than 25° C.
22. The method according to claim 18 wherein the radiopaque species is a compound of the formula IV:
wherein:
A is selected from —CHO, —CHOR 1 OR 2 —CHOR 1 OH, —CHSR 1 OH or —CHSR 1 SR 2 wherein R 1 and R 2 are independently selected from C 1-4 alkyl;
Z is a linking group, or is absent; if Z is present, then Z is C 1-6 alkylene, C 1-6 alkoxylene or C 1-6 alkoxyalkylene; and
Hal is 1,2,3 or 4 covalently attached iodines.
23. The method according to claim 18 wherein the radiopaque species is 2,3,5-triiodobenzaldehyde, 2,3,4,6-tetraiodobenzyaldehyde or 2-(2,4,6-triiodophenoxy)acetaldehyde.
24. Hydrogel polymer microspheres according to claim 1 , wherein the hydrogel polymer is PVA or a copolymer of PVA.
25. Polymer microspheres comprising:
a PVA polymer backbone including at least two pendant chains having cross-linkable ethylenically unsaturated functional groups which are cross linked by 2-acrylamido-2-methylpropanesulfonate, the PVA polymer backbone having a structure according to the general formula:
and;
a therapeutic agent selected from irinotecan, topotecan, doxorubicin, epirubicin, sorafenib, sunitinib, vandetanib, and miriplatin.
26. Polymer microspheres according to claim 25 , wherein the polymer is a hydrogel.
27. Polymer microspheres according to claim 25 , wherein the polymer is an acrylamido polyvinyl alcohol-coacrylamido-2-methylpropane sulfonate hydrogel.
28. Polymer microspheres according to claim 25 , wherein the therapeutic agent is electrostatically held within the hydrogel matrix.