Silicon-based anode material for lithium ion battery
A porous reduced silica fiber material has a diameter of about 0.1 to about 20 microns and a surface area of about 5 m 2 /g to about 400 m 2 /g. The porous reduced fiber material may be used to form an electrode having a high capacity and improved cycle life over comparable commercial silicon electrodes.
1. A porous reduced silica fiber having a diameter of about 0.1 to about 20 microns, a surface area of about 5 m 2 /g to about 400 m 2 /g, and a porosity of about 0.01 cm 3 /g to about 1.5 cm 3 /g,
wherein the porous reduced silica fiber comprises SiO x where x=0-2; and
wherein the porous reduced silica fiber comprises greater than about 20 weight percent silicon.
2. The porous reduced silica fiber of claim 1 , having a diameter of about 2 to about 15 microns.
3. The porous reduced silica fiber of claim 1 , having a surface area of about 30 m 2 /g to about 300 m 2 /g.
4. The porous reduced silica fiber of claim 1 , having a porosity of about 0.1 cm 3 /g to about 0.7 cm 3 /g.
5. The porous reduced silica fiber of claim 1 , having a median pore diameter of about 1 nm to about 90 nm.
6. The porous reduced silica fiber of claim 1 , having pore diameters of about 0.1 nm to about 150 nm.
7. The porous reduced silica fiber of claim 6 , having pore diameters of about 1 nm to about 100 nm.
8. A process for producing the porous reduced silica fiber of claim 1 , comprising:
providing a solution comprising a silica precursor, a polymer, and a surface active agent;
fiberizing the solution to produce fibers;
heating the fibers to produce silica-based precursor fibers;
subjecting the silica-based precursor fibers to a magnesiothermic reduction to remove at least some oxygen from the silica-based precursor fibers and to produce reduced silica fibers; and
washing the reduced silica fibers in an acid to remove magnesium-bearing reaction products and to produce the porous reduced silica fiber.
9. A process for producing the porous reduced silica fiber of claim 1 , comprising:
providing a melt comprising silica (SiO 2 ) and at least one of sodium oxide (Na 2 O), boron trioxide (B 2 O 3 ), lithium oxide (Li 2 O), calcium oxide (CaO) and magnesia (MgO);
fiberizing the melt to produce fibers;
treating the fibers to remove at least a portion of non-silica components and produce silica-based precursor fibers;
subjecting the silica-based precursor fibers to a magnesiothermic reduction to remove at least some oxygen from the silica-based precursor fibers and to produce reduced silica fibers; and
washing the reduced silica fibers in an acid to remove magnesium-bearing reaction products and to produce the porous reduced silica fiber.
10. A battery electrode comprising a binder and the porous reduced silica fiber of claim 1 .
11. The battery electrode of claim 10 , having a Coulombic efficiency of about 30% to about 100%.
12. The battery electrode of claim 10 , having a capacity ratio cycle 3/cycle 1 of about 0.4 to about 1.0.
13. The battery electrode of claim 10 , having a capacity ratio cycle 10/cycle 1 of about 0.1 to about 1.0.
14. A lithium ion battery comprising the electrode of claim 10 .
15. A porous reduced silica fiber having a diameter of about 0.1 to about 20 microns, a surface area of about 5 m 2 /g to about 400 m 2 /g, and a porosity of about 0.01 cm 3 /g to about 1.5 cm 3 /g,
wherein the porous reduced silica fiber comprises SiO x where x=0-2; and
wherein the porous reduced silica fiber comprises (i) greater than about 20 weight percent silicon and (ii) silicon dioxide.
16. The porous reduced silica fiber of claim 15 , having a surface area of about 30 m 2 /g to about 300 m 2 /g.
17. The porous reduced silica fiber of claim 15 , having a porosity of about 0.1 cm 3 /g to about 0.7 cm 3 /g.
18. The porous reduced silica fiber of claim 15 , having a median pore diameter of about 1 nm to about 90 nm.
19. A battery electrode comprising a binder and the porous reduced silica fiber of claim 15 .
20. A lithium ion battery comprising the electrode of claim 19 .
21. A porous reduced silica fiber consisting essentially of SiO x where x=0-2, wherein the porous reduced silica fiber has a diameter of about 0.1 to about 20 microns, a surface area of about 5 m 2 /g to about 400 m 2 /g, a porosity of about 0.01 cm 3 /g to about 1.5 cm 3 /g, and greater than about 20 weight percent silicon.