Weldability improvements in advanced high strength steel
This disclosure relates to weldability of steel alloys that provide weld joints which retain hardness values in a heat affected zone adjacent to a fusion zone and which also have improved resistance to liquid metal embrittlement due to the presence of zinc coatings.
1. A method for joining high strength sheet steel comprising:
a. supplying a metal alloy consisting essentially of 70 to 90 atomic % iron, one or both of Ni and Cu, and at least two elements selected from Si, Mn, Cr, and C, and inevitable impurities, and melting said alloy and cooling at a rate of <250 K/s and solidifying to a thickness of 25 mm up to 500 mm and forming an alloy having a melting point Tm;
b. processing said alloy into sheet form with thickness up to 5.0 mm with the sheet exhibiting a total elongation 10.0 to 75.0%, a yield strength 250 to 1200 MPa, a tensile strength 700 to 1700 MPa, and a hardness H1;
c. welding said sheet self-to-self by heating and forming: (i) a fusion zone in said sheet at a temperature T1 above the alloy Tm, the fusion zone containing >50 volume % austenite; and (ii) a heat affected zone in said sheet at a temperature T2 that is less than the alloy Tm;
d. cooling said sheet and forming a hardness H2 in said heat affected zone of said sheet wherein H2=H1+/−100 HV.
2. The method of claim 1 wherein said sheet has a thickness of 0.1 mm to 5.0 mm.
3. The method of claim 1 wherein said alloy formed in step (a) exhibits a Tm from 1250 and 1650° C.
4. The method of claim 1 wherein said alloy formed in step (b) exhibits H1 from 150 to 650 HV.
5. The method of claim 1 wherein said welding comprises one or more of resistance spot welding, resistance seam welding, upset welding, laser beam welding, or electron beam welding.
6. The method of claim 1 in step (c) wherein T1 is ≥1250° C. and less than 2500° C.
7. The method of claim 1 in step (c) wherein T2 is ≥400° C. and less than the melting temperature Tm of the alloy.
8. The method of claim 1 wherein said alloy contains both nickel and copper.
9. The method of claim 1 further comprising positioning said sheet formed in step (d) in a vehicular frame, vehicular chassis, or vehicular panel.
10. The method of claim 1 further comprising positioning said sheet formed in step (d) in a storage tank, freight car, or railway tank car including tank, jacket, or headshield.
11. A method for joining high strength sheet steel with other steel grades comprising:
a. supplying a metal alloy consisting essentially of 70 to 90 atomic % iron, one or both of Ni and Cu, and at least two elements selected from Si, Mn, Cr, and C, and inevitable impurities, and melting said alloy and cooling at a rate of <250 K/s and solidifying to a thickness of 25 mm up to 500 mm and forming an alloy having a melting point Tm;
b. processing said alloy into sheet form with thickness up to 5.0 mm with the sheet exhibiting a total elongation 10.0 to 75.0%, yield strength 250 to 1200 MPa, tensile strength 700 to 1700 MPa, and a hardness H1;
c. welding said sheet to another steel by heating and forming: (i) a fusion zone in said sheet at a temperature T1 above the alloy Tm, said fusion zone containing >50 volume % austenite; and (ii) a heat affected zone in said sheet at a temperature T2 that is less than the alloy Tm; and
d. cooling said sheet and forming a hardness H3 in said heat affected zone of said sheet wherein H3=H1+/−125 HV.
12. The method of claim 11 wherein said sheet has a thickness of 0.1 mm to 5.0 mm.
13. The method of claim 11 wherein said alloy formed in step (a) exhibits a Tm from 1250 and 1650° C.
14. The method of claim 11 wherein said alloy formed in step (b) exhibits H1 from 150 to 650 HV.
15. The method of claim 11 wherein said welding comprises one or more of resistance spot welding, resistance seam welding, upset welding, laser beam welding, or electron beam welding.
16. The method of claim 11 in step (c) wherein T1 is ≥1250° C. and less than 2500° C.
17. The method of claim 11 in step (c) wherein T2 is ≥400° C. and less than the melting temperature Tm of the alloy.
18. The method of claim 11 wherein said alloy contains both nickel and copper.
19. The method of claim 11 further comprising positioning the sheet formed in step (d) in a vehicular frame, vehicular chassis, or vehicular panel.
20. The method of claim 11 further comprising positioning the sheet formed in step (d) in a storage tank, freight car, or railway tank car including tank, jacket, or headshield.
21. A method for joining a coated high strength sheet steel comprising:
a. supplying a metal alloy consisting essentially of 70 to 90 atomic % iron, one or both of Ni and Cu, and at least two elements selected from Si, Mn, Cr, and C, and inevitable impurities, and melting said alloy and cooling at a rate of <250 K/s and solidifying to a thickness of 25 mm up to 500 mm and forming an alloy having a melting point Tm;
b. processing said alloy into sheet form with thickness L1, with the sheet exhibiting a total elongation 10.0 to 75.0%, a yield strength 250 to 1200 MPa, a tensile strength 700 to 1700 MPa;
c. applying a zinc containing coating to said alloy sheet and forming a coated sheet;
d. welding said coated sheet self-to-self or to other steels by heating and forming a fusion zone that contains >50 volume % austenite, wherein said other steels have uncoated surfaces or surfaces with zinc containing coatings;
e. cooling to form a weld which: (1) is crack free; or (2) contains one or more cracks with the depth of the largest crack at L2, which is ≤15% of sheet thickness L1.
22. The method of claim 21 wherein said alloy formed in step (a) exhibits a Tm from 1250 and 1650° C.
23. The method of claim 21 wherein said coated alloy sheet in step (b) has a thickness of up to 5.0 mm.
24. The method of claim 21 wherein said alloy contains both nickel and copper.
25. The method of claim 21 wherein said alloy in step (c) has a zinc containing coating which is from 1 to 50 μm thick.
26. The method of claim 21 wherein said welding comprises one or more of resistance spot welding, resistance seam welding, upset welding, laser beam welding, or electron beam welding.
27. The method of claim 21 wherein said alloy containing a weld formed in step (e) exhibits a maximum crack depth L2 of 75 to 1500 μm.
28. The method of claim 21 wherein said cooled alloy containing a weld formed in step (e) is positioned in a vehicular frame, vehicular chassis, or vehicular panel.
29. The method of claim 21 wherein said cooled alloy containing a weld formed in step (e) is positioned in a storage tank, freight car, or railway tank car including tank, jacket, or headshield.