Aqueous dispersion containing silicon dioxide and trimethyl-1,6-hexamethylendiamine
An aqueous dispersion can be used to prepare a lacquer preparation. The aqueous dispersion includes silicon dioxide and at least one of 2,2,4-trimethyl-1,6-hexamethylenediamine and 2,4,4-trimethyl-1,6-hexamethylenediamine.
1. An aqueous dispersion, comprising: from 1% to 30% by weight of silicon dioxide and at least one member selected from the group consisting of 2,2,4-trimethyl-1,6-hexamethylenediamine and 2,4,4-trimethyl-1,6-hexamethylenediamine,
wherein the aqueous dispersion has a pH of 10 to 12,
wherein the silicon dioxide is a pyrogenic silicon dioxide, and
wherein the silicon dioxide has a tamped density of up to 400 g/L, determined according to DIN ISO 787-11:1995.
2. The aqueous dispersion according to claim 1 , comprising from 0.01% to 10% by weight of 2,2,4-trimethyl-1,6-hexamethylenediamine, 2,4,4-trimethyl-1,6-hexamethylenediamine, or a combination thereof.
3. The aqueous dispersion according to claim 1 , wherein the silicon dioxide is in the form of particles having a numerical average particle size d 50 of not more than 300 nm.
4. The aqueous dispersion according to claim 1 , wherein a molar ratio of silicon dioxide to 2,2,4-trimethyl-1,6-hexamethylenediamine, 2,4,4-trimethyl-1,6-hexamethylenediamine, or the combination thereof, in the dispersion is from 5 to 100.
5. The aqueous dispersion according to claim 1 , wherein a molar ratio of silicon dioxide to water in the dispersion is from 0.003 to 0.5.
6. The aqueous dispersion according to claim 1 , wherein the silicon dioxide has a methanol wettability of less than 20% by weight of methanol in a methanol/water mixture.
7. The aqueous dispersion according to claim 1 , wherein the silicon dioxide has a hydroxyl density of 1.2 to 5.4 OH/nm 2 .
8. The aqueous dispersion according to claim 3 , wherein the silicon dioxide particles have a BET surface area of 20 to 500 m 2 /g.
9. The aqueous dispersion according to claim 1 , which comprises 2,2,4-trimethyl-1,6-hexamethylenediamine and 2,4,4-trimethyl-1,6-hexamethylenediamine, wherein a molar ratio of 2,2,4-trimethyl-1,6-hexamethylenediamine to 2,4,4-trimethyl-1,6-hexamethylenediamine is from 0.8 to 1.2.
10. A process for producing the dispersion according to claim 1 , the process comprising: stirring the mixture comprising silicon dioxide, water and at least one member selected from the group consisting of 2,2,4-trimethyl-1,6-hexamethylenediamine and 2,4,4-trimethyl-1,6-hexamethylenediamine.
11. A process for adjusting a rheological property of a composition, the process comprising: adding the aqueous dispersion according to claim 1 to the composition, wherein the composition is selected from the group consisting of an automotive hydrofiller, a coating composition, a water-based UV curable formulation, and a clear lacquer.
12. An additive to hydrofillers, comprising: the aqueous dispersion according to claim 1 .
13. The aqueous dispersion according to claim 1 , comprising from 0.5% to 5% by weight of 2,2,4-trimethyl-1,6-hexamethylenediamine, 2,4,4-trimethyl-1,6-hexamethylenediamine, or a combination thereof and 50% to 98.5% by weight water.
14. The aqueous dispersion according to claim 1 , wherein weight proportion of the silicon dioxide is at least 90% by weight based on solids content of the aqueous dispersion.
15. The aqueous dispersion according to claim 1 , comprising 5 to 30% by weight of the silicon dioxide.
16. The aqueous dispersion according to claim 1 , comprising 10 to 30% by weight of the silicon dioxide.
17. The aqueous dispersion according to claim 1 , wherein the silicon dioxide has a tamped density of 40 to 100 g/L, determined according to DIN ISO 787-11:1995.