Low biopersistence inorganic fiber free of crystalline silica
An inorganic fiber containing silica, alumina, one or more alkali metal oxides, and one or more of alkaline earth metal oxides, transition metal oxides, or lanthanide series metal oxides. The inorganic fiber exhibits good thermal performance at use temperatures of 1260° C. and greater, retains mechanical integrity after exposure to the use temperatures, is free of crystalline silica upon devitrification, is alkali flux resistant, exhibits low bio-persistence in an acidic medium, and exhibits low dissolution in a neutral medium. Also provided are thermal insulation products incorporating the inorganic fibers, a method for preparing the inorganic fiber and a method of thermally insulating articles using thermal insulation prepared from the inorganic fibers.
1. An inorganic fiber comprising the fiberization product of
(i) 15 to 50 mol percent silica;
(ii) 10 to 28 mol percent alumina;
(iii) 16.7 to 35 mol percent of an alkali metal oxide; and
(iv) 15 to 35 mol percent of at least one alkaline earth metal oxide;
wherein the amount of silica+alumina+alkali metal oxide is 80 mol percent or less;
wherein a molar ratio of alkali metal oxide to the alumina is from 1.25 to 2;
wherein the amount of alumina+alkali metal oxide is 30 mol percent or greater; and
wherein the inorganic fiber exhibits a linear shrinkage after exposure to 1260° C. for 24 hours of 5% or less.
2. The inorganic fiber of claim 1 , wherein the amount of alumina is 13 mol percent or greater.
3. The inorganic fiber of claim 1 , wherein the amount of alumina+alkali metal oxide is 34 mol percent or greater.
4. The inorganic fiber of claim 3 , wherein the amount of alumina+alkali metal oxide is 34 mol percent or greater, wherein the amount of alumina is 14 mol percent or greater.
5. The inorganic fiber of claim 1 , wherein the molar ratio of alkali metal oxide to the alumina is from 1.3 to 2.
6. The inorganic fiber of claim 1 , comprising the fiberization product of
(i) 15 to 50 mol percent silica;
(ii) 10 to 28 mol percent alumina;
(iii) 16.7 to 35 mol percent dipotassium oxide, and
(iv) 15 to 35 mol percent of at least one alkaline earth metal oxide.
7. The inorganic fiber of claim 1 , comprising the fiberization product of
(i) 15 to 50 mol percent silica;
(ii) 10 to 28 mol percent alumina;
(iii) 16.7 to 35 mol percent of the alkali metal oxide; and
(iv) 15 to 35 mol percent of magnesium oxide.
8. The inorganic fiber of claim 1 , comprising the fiberization product of
(i) 15 to 50 mol percent silica;
(ii) 10 to 28 mol percent alumina;
(iii) 16.7 to 35 mol percent of dipotassium oxide; and
(iv) 15 to 35 mol percent of magnesium oxide.
9. The inorganic fiber of claim 1 , wherein said fiber does not exhibit crystalline silica phase as measured by x-ray diffraction (XRD) after exposure to 1260° C. for 24 hours.
10. The inorganic fiber of claim 9 , wherein said inorganic fiber exhibits a 6 hour dissolution rate in an acidic medium that is greater than the 6 hour dissolution rate in a neutral or near neutral medium.
11. A thermal insulation or fire protection material prepared from a plurality of the inorganic fibers of claim 1 , the material selected from blankets, blocks, boards, caulking compositions, cement compositions, coatings, felts, mats, moldable compositions, modules, papers, pumpable compositions, putty compositions, sheets, tamping mixtures, vacuum cast shapes, vacuum cast forms, or woven textiles, braids, cloths, fabrics, ropes, tapes, sleeving, and wicking.
12. A method for making the inorganic fiber comprising:
combining raw material ingredients comprising
i) 15 to 50 mol percent silica,
(ii) 10 to 35 mol percent alumina,
(iii) 15 to 28 mol percent of an alkali metal oxide, and
(iv) 16.7 to 35 mol percent of at least one alkaline earth metal oxide to form a molten melt of raw material ingredients; and
producing fibers from the molten melt;
wherein the amount of silica+alumina+alkali metal oxide is 80 mol percent or less;
wherein a molar ratio of alkali metal oxide to the alumina is from 1.25 to 2;
wherein the amount of alumina+alkali metal oxide is 30 mol percent or greater; and
wherein the inorganic fiber exhibits a linear shrinkage after exposure to 1260° C. for 24 hours of 5% or less.
13. A method of thermally insulating an article at temperatures of 1260° C. and greater, comprising disposing on, in, near, or around the article to be thermally insulated, a thermal insulation material comprising a plurality of inorganic fibers of claim 1 .
14. A method of thermally insulating an article at temperatures of 1400° C. and greater, or providing fire protection to said article, comprising disposing on, in, near or around the article to be thermally insulated, a thermal insulation material comprising a plurality of inorganic fibers of claim 1 .