Process for producing nanostructured metal substrates for use in Surface Enhanced Raman Spectroscopy or similar applications
A framework of copper oxide dendrites is formed on a copper substrate, and these are then coated or plated with silver, gold, or an equivalent metal to create metal-coated dendrites with nano-structures, favorably in range of 50 to 200 nanometers. The framework of metal-coated dendrites are well suited for use in surface-enhanced Raman spectroscopy and other practical applications.
1. Process for forming a nano-scale substrate suitable for use in Surface Enhanced Raman Spectroscopy (SERS) and/or other similar Raman spectroscopy applications, comprising:
starting with a substrate having thereon a layer of copper;
subjecting the copper layer to oxidation in a process bath to form a layer of copper oxide dendrites thereon having sizes on the order of up to 100 μm and of one μm;
cleaning the substrate and the copper oxide dendrites;
depositing on the copper oxide dendrites a coating of a noble metal; and
cleaning and rinsing the noble-metal coating to render the substrate and coated dendrites suitable for SERS and/or other suitable Raman spectroscopy applications.
2. The process of claim 1 wherein said step of starting with a layer of copper is followed by a step of chemically polishing said layer of copper.
3. The process of claim 1 wherein step of subjecting the copper layer to oxidation in a process bath includes employing an aqueous reagent bath with sulfur compounds and oxidizers.
4. The process of claim 1 wherein said step of subjecting the copper layer to oxidation in a process bath results in dendrites in a plurality of sizes from less than one micron up to a hundred microns.
5. The process of claim 1 wherein said subjecting the copper layer to oxidation in a process bath is carried out at an elevated temperature of about 90° C.
6. The process of claim 1 wherein said noble metal is selected from the group consisting of Ag, Au, Pa and Pt.
7. The process of claim 1 wherein said noble metal consists of one or more from the group consisting of Ag, Au, Sn, Ni, Cu, Pt, Pa, Rh and Zn.