Low-temperature radical polymerisation of alkoxyamines
View Patent ↗The present invention relates to a process for the radical polymerization of alkoxyamines at low temperature, typically at temperatures as low as −50° C., in the presence of a nitroxide reducing agent or photoinitiator.
1. A radical polymerization process comprising the steps of:
a) providing a mixture comprising:
at least one monomer;
at least one alkoxyamine;
at least one compound that activates the at least one alkoxyamine, wherein the at least one compound that activates the alkoxyamine is selected from the group consisting of at least one nitroxide reducing agent, at least one photoinitiator, and mixtures thereof;
b) polymerizing the mixture at a temperature of between 0° C. and 50° C.
2. The radical polymerization process according to claim 1 , wherein the at least one alkoxyamine is monofunctional.
3. The radical polymerization process according to claim 1 , wherein the at least one alkoxyamine is multifunctional.
4. The radical polymerization process according to claim 1 wherein the at least one alkoxyamine is a macromolecular alkoxyamine.
5. The radical polymerization process according to claim 1 , wherein the at least one nitroxide reducing agent is a radical.
6. The radical polymerization process according to claim 1 , wherein the nitroxide reducing agent comprises at least one radical initiator, wherein at least one radical is obtained from the decomposition of the radical initiator.
7. The radical polymerization process according to claim 1 , wherein the nitroxide reducing agent comprises at least one peroxide and at least one amine, wherein at least one radical is obtained from the decomposition of the peroxide in the presence of the at least one amine.
8. The radical polymerization process according to claim 7 , wherein the at least one peroxide is benzoyl peroxide.
9. The radical polymerization process according to claim 7 wherein the at least one amine is dimethyl-para-toluidine.
10. The radical polymerization process according to claim 1 wherein the nitroxide reducing agent comprises an initiator, wherein the initiator generates free radicals thermally.
11. The radical polymerization process according to claim 1 , wherein the polymerization is performed in the presence of a host material.
12. The radical polymerization process according to claim 1 , wherein the host material is selected from the group consisting of woven fibers, nonwoven fibers, polyester, polyurethane, and epoxy resins.
13. The radical polymerization process according to claim 1 , wherein the radical polymerization process is used to manufacture bonding agents, composite parts, varnishes, coatings, or 3D printed articles.
14. An article of manufacture, wherein the article is manufactured according to the radical polymerization process of claim 1 .
15. An article of manufacture, wherein the article is manufactured according to the radical polymerization process of claim 11 .
16. An article of manufacture wherein the article is manufactured according to the radical polymerization process of claim 12 .
17. The radical polymerization process according to claim 11 wherein the radical polymerization process is used to manufacture bonding agents, composite parts, varnishes, coatings, or 3D printed articles.
18. The radical polymerization process according to claim 12 wherein the radical polymerization process is used to manufacture bonding agents, composite parts, varnishes, coatings, or 3D printed articles.