Aluminum based composite material, electric wire using the same, and manufacturing method of aluminum based composite material
An aluminum based composite material includes an aluminum parent phase and dispersions dispersed in the aluminum parent phase and formed such that a portion or all of additives react with aluminum in the aluminum parent phase, an average particle diameter of the dispersions is 20 nm or less, a content of the dispersions is 0.25% by mass or more and 0.72% by mass or less in terms of carbon amount, and an interval between the dispersions adjacent to each other is 210 nm or less.
1. An aluminum based composite material comprising an aluminum parent phase and dispersions dispersed in the aluminum parent phase and the dispersions are formed by at least a portion or all of additives reacting with aluminum in the aluminum parent phase, wherein
an average particle diameter of the dispersions is 20 nm or less,
a content of the dispersions is 0.25% by mass or more and 0.50% by mass or less in terms of carbon amount,
an average interval between the dispersions adjacent to each other is 210 nm or less and is calculated from the average particle diameter and the content of the dispersions in a cross-section of the aluminum based composite material, and
the aluminum based composite material has a conductivity of 58% IACS or more and a tensile strength of 250 MPa or more.
2. The aluminum based composite material according to claim 1 , wherein the additives comprise at least one of carbon nanotubes, carbon nanohorns, carbon black, and boron carbide.
3. The aluminum based composite material according to claim 1 ,
wherein the additives further comprise boron nitride.
4. An electric wire comprising the aluminum based composite material according to claim 1 .
5. A manufacturing method of the aluminum based composite material according to claim 1 , the method comprising:
mixing an aluminum powder having purity of 99% by mass or more with the additives to obtain a mixed powder in which an interval between the additives adjacent to each other is 300 nm or less;
preparing a green compact by compacting the mixed powder; and
heating the green compact at a temperature of 600 to 660° C. to react a portion or all of the additives with aluminum in the aluminum powder, so as to disperse the dispersions formed of aluminum carbide inside the aluminum parent phase.