COMPOSITION FOR FORMING SOLAR CELL ELECTRODE AND ELECTRODE PREPARED USING THE SAME
A composition for solar cell electrodes and a solar cell electrode fabricated using the composition, the composition including a conductive powder; a glass frit; and an organic vehicle, wherein the glass frit has a reaction index (RI) of about 0.5 to about 1.0, as calculated according to Equation 1: Reaction index (RI)= Ib/Ia <Equation 1> wherein, in Equation 1, Ia denotes a maximum peak intensity measured on a specimen at 20.5° to 20.7° (2θ) by XRD analysis, the specimen being obtained by mixing the glass frit with Si 3 N 4 powder in a weight ratio of 1:1 to prepare pellets, followed by heat-treatment at 800° C. for 10 minutes, and Ib denotes a maximum peak intensity measured on the specimen at 20.75° to 20.95° (2θ) by XRD analysis.
1 . A composition for solar cell electrodes, the composition comprising:
a conductive powder;
a glass frit; and
an organic vehicle,
wherein the glass frit has a reaction index (RI) of about 0.5 to about 1.0, as calculated according to Equation 1:
Reaction index (RI)= Ib/Ia <Equation 1>
wherein, in Equation 1,
Ia denotes a maximum peak intensity measured on a specimen at 20.5° to 20.7° (2θ) by XRD analysis, the specimen being obtained by mixing the glass frit with Si 3 N 4 powder in a weight ratio of 1:1 to prepare pellets, followed by heat-treatment at 800° C. for 10 minutes, and
Ib denotes a maximum peak intensity measured on the specimen at 20.75° to 20.95° (2θ) by XRD analysis.
2 . The composition as claimed in claim 1 , wherein the glass frit includes tellurium (Te), lithium (Li), zinc (Zn), bismuth (Bi), lead (Pb), sodium (Na), phosphorus (P), silver (Ag), germanium (Ge), gallium (Ga), cerium (Ce), iron (Fe), silicon (Si), tungsten (W), magnesium (Mg), molybdenum (Mo), cesium (Cs), strontium (Sr), titanium (Ti), tin (Sn), indium (In), vanadium (V), barium (Ba), nickel (Ni), copper (Cu), potassium (K), arsenic (As), cobalt (Co), zirconium (Zr), manganese (Mn), aluminum (Al), or boron (B).
3 . The composition as claimed in claim 1 , wherein the glass frit includes a lead (Pb)-tellurium (Te)-lithium (Li) glass frit, a lead (Pb)-tellurium (Te)-lithium (Li)-zinc (Zn) glass frit, a bismuth (Bi)-tellurium (Te)-lithium (Li) glass frit, or a bismuth (Bi)-tellurium (Te)-lithium (Li)-zinc (Zn) glass frit.
4 . The composition as claimed in claim 1 , wherein the composition includes:
about 60 wt % to about 95 wt % of the conductive powder;
about 0.1 wt % to about 20 wt % of the glass fit; and
about 1 wt % to about 30 wt % of the organic vehicle.
5 . The composition as claimed in claim 1 , further comprising a dispersant, a thixotropic agent, a plasticizer, a viscosity stabilizer, an anti-foaming agent, a pigment, a UV stabilizer, an antioxidant, or a coupling agent.
6 . A solar cell electrode fabricated using the composition for solar cell electrodes as claimed in claim 1 .