Method and apparatus for releasing molded article from mold
In the method and the apparatus for releasing a molded article from a mold according to the embodiments, the lateral of the molded article in the mold is pressed, so that it is possible to minimize the damage of the mold and the molded article at the time of the release, while the amount of a mold release agent used is minimized.
1. A method for releasing a molded article from a mold, which comprises fixing the mold containing the molded article to a support; and
pressing the lateral of the molded article in the fixed mold with a presser,
wherein the pressing is applied to the lateral of the molded article in the mold such that the lateral of the molded article is compressed by 0.1 mm to 5.0 mm,
wherein the modulus at 20° C. to 70° C. of the mold is 50,000 MPa to 70,000 MPa, the modulus of the molded article is 500 MPa to 5,000 MPa, and the ratio of the modulus of the mold to the modulus of the molded article is 30:1 to 70:1,
wherein the pressing is carried out at 60° C. to 120° C.; and
wherein a damage ratio of the mold is 0% to 5%, and a release ratio of the molded article is 95% to 100%.
2. The method of claim 1 , which has a damage ratio of the molded article of less than 8%.
3. The method of claim 1 , wherein the molded article comprises an internal release agent.
4. The method of claim 1 , wherein the mold is a glass mold, and the molded article is a plastic lens.