Alloyed hot-dip galvanized steel sheet and method of manufacturing the same
Provided is an alloyed hot-dip galvanized steel sheet including a base steel sheet, the base steel sheet containing a given amount of C, Si, Mn, and other elements. The alloyed hot-dip galvanized steel sheet is provided with an alloyed hot-dip galvanized layer on a surface of the base steel sheet, the alloyed hot-dip galvanized layer containing, in mass %, Fe: more than or equal to 5% and less than or equal to 15%, and having a thickness of more than or equal to 3 μm and less than or equal to 30 μm. The alloyed hot-dip galvanized steel sheet includes an A layer immediately under the surface of the base steel sheet, the A layer being formed in the base steel sheet and having a thickness of more than or equal to 2 μm and less than or equal to 20 μm from the surface of the base steel sheet, containing more than or equal to 50 vol % of a ferrite structure, and containing more than or equal to 90 mass % of unoxidized Fe, less than or equal to 10 mass % of a total of contents of oxides of Fe, Si, Mn, P, S, and Al, and less than 0.05 mass % of C.
1. A method of manufacturing an alloyed hot-dip galvanized steel sheet using a base steel material, the base steel material containing, in mass %,
C: more than or equal to 0.05% and less than or equal to 0.50%,
Si: more than or equal to 0.2% and less than or equal to 3.0%,
Mn: more than or equal to 0.5% and less than or equal to 5.0%,
Al: more than or equal to 0.001 and less than or equal to 1.0%,
P: less than or equal to 0.1%,
S: less than or equal to 0.01%,
N: less than or equal to 0.01%, and
the balance including Fe and inevitable impurities,
the method comprising:
performing casting, hot-rolling, pickling, and cold rolling to thereby produce the base steel material;
subjecting the base steel material to a hot-dip galvanizing treatment by performing, using a continuous hot-dip galvanizing plant equipped with a heating furnace and a soaking furnace, an annealing treatment in which a temperature of the base steel material is increased within a range of higher than or equal to 500° C. and lower than or equal to 950° C. in the heating furnace and the soaking furnace; and
subjecting the base steel material to an alloying treatment at higher than or equal to 440° C. and lower than or equal to 600° C.,
wherein the annealing treatment is performed under the following conditions:
conditions of the heating furnace: an all radiant tube type heating furnace is used, a time period that the temperature of the base steel material is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. is 100 seconds to 1000 seconds, an atmosphere of the heating furnace contains hydrogen, water vapor, and nitrogen, a logarithm log(P H2O /P H2 ) of a value obtained by dividing a partial water vapor pressure (P H2O ) by a partial hydrogen pressure (P H2 ) is more than or equal to −4.0 and less than −2.0, and a hydrogen concentration is more than or equal to 3 vol % and less than or equal to 30 vol %; and
conditions of the soaking furnace: a time period that the temperature of the base steel material is in the range of higher than or equal to 500° C. and lower than or equal to 950° C. is 100 seconds to 1000 seconds, an atmosphere of the soaking furnace contains hydrogen, water vapor, and nitrogen, a logarithm log(P H2O /P H2 ) of a value obtained by dividing a partial water vapor pressure (P H2O ) by a partial hydrogen pressure (P H2 ) is more than or equal to −8.0 and less than −4.0, and a hydrogen concentration is more than or equal to 3 vol % and less than or equal to 30 vol %.
2. A method of manufacturing the alloyed hot-dip galvanized steel sheet according to claim 1 ,
wherein the base steel material further contains one or more of, in mass %,
Cr: more than or equal to 0.05% and less than or equal to 1.0%,
Ni: more than or equal to 0.05% and less than or equal to 1.0%,
Cu: more than or equal to 0.05% and less than or equal to 1.0%,
Nb: more than or equal to 0.005% and less than or equal to 0.3%,
Ti: more than or equal to 0.005% and less than or equal to 0.3%,
V: more than or equal to 0.005% and less than or equal to 0.5%,
B: more than or equal to 0.0001% and less than or equal to 0.01%,
Ca: more than or equal to 0.0005% and less than or equal to 0.04%,
Mg: more than or equal to 0.0005% and less than or equal to 0.04%,
La: more than or equal to 0.0005% and less than or equal to 0.04%,
Ce: more than or equal to 0.0005% and less than or equal to 0.04%, and
Y: more than or equal to 0.0005% and less than or equal to 0.04%.