Thermoplastic polymer film with interpenetrating polymer network

1. A multilayer thermoplastic film comprising:

a first layer having a thickness of about 0.2 mil to about 3 mil and comprising an interpenetrating network, wherein the interpenetrating network comprises:

a first thermoplastic polymer, wherein the first thermoplastic polymer is a cured polymer selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof,

crosslinked components, wherein the crosslinked components are selected from the group consisting of acrylates, methacrylates, and allylic isocyanurates, and

a photoinitiator, wherein the crosslinked components and the photoinitiator are combined with the cured polymer to form the interpenetrating network; and

a second layer comprising one or more layers of a second thermoplastic polymer, wherein the second thermoplastic polymer is selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof.

2. The multilayer thermoplastic film of claim 1 , wherein the crosslinked components are selected from the group consisting of triallyl isocyanurate (TAIC), trimethylolpropane triacrylate (TMPTA), di-trimethylolpropane tetraacrylate (DTMPTA), and tri-functional methacrylate.

3. The multilayer thermoplastic film of claim 1 , wherein the photoinitiator is selected from the group consisting of 1-hydroxy-cyclohexyl-phenyl ketone, a mixture of oxy-phenyl-acetic acid 2-[2 oxo-2-acetoxy-ethoxy]-ethyl ester and oxy-phenyl-acetic 2-[2-hydroxy-ethoxy]-ethyl ester, phosphine oxide, phenylbis(2,4,6-trimethylbenzoyl) phosphine oxide, diphenyl (2,4,6-trimethylbenzoyl)-phosphine oxide (TPO), methylbenzoylformate (MBF), oligo[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone], 2,2-dimethoxy-1,2-diphenyl-ethanone (BDK), ethyl phenyl (2,4,6-trimethylbenzoyl) phosphinate, ethyl (2,4,6-trimethylbenzoyl)-phenyl-phosphinate, a mixture of 2 hydroxy-2-methylpropiophenone, ethyl (2,4,6-trimethylbenzoyl) (phenylphosphinate and oligo[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone]), difunctional alpha-hydroxy ketone, oligo(2-hydroxy-2-methyl-1-(4-(1-methylvinyl)phenyl)propanone), a blend of diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide and 2-hydroxy-2-methyl-1-phenyl-propanone, a blend of piparazino based aminoalkylphenone and pentaerythritol tetraacrylate (PPTTA), polyethylene glycol di(beta-4-[4-(2-dimethylamino-2-benzyl) butanoyl phenyl]piperazine)propionate, 2,3-dihydro-6-(2-hydroxy-2-methyl-1-oxopropyl)-1,1,3-trimethyl-3-[4-(2-hydroxy-2-methyl-1-oxopropyl)phenyl]-1H-indene; a mixture of 2,3-dihydro-5-(2-hydroxy-2-methyl-1-oxopropyl)-1,1,3-trimethyl-3-[4-(2-hydroxy-2-methyl-1-oxopropyl)phenyl]-1H-indene and 2-hydroxy-2-methylpropiophenone, 70% oligo[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone] mixed with 30% 2-hydroxy-2-methylpropiophenone, diester of carboxymethoxy-benzophenone and polytetramethyleneglycol 250, and a mixture of 1-propanone, 1,1′-oxydi-4,1-phenlene)-bis(2-hydroxy-2-methyl- and 1-hydroxycyclohexyl phenyl ketone).

4. The multilayer thermoplastic film of claim 1 , further comprising a heat stabilizer.

5. The multilayer thermoplastic film of claim 1 , wherein the second layer has a thickness of about 3 mil to about 8 mil.

6. The multilayer thermoplastic film of claim 1 , wherein the first layer comprises about 65% to about 75% by weight of the first thermoplastic polymer and about 20% to about 30% by weight of the crosslinked components.

7. The multilayer thermoplastic film of claim 1 , wherein the first thermoplastic polymer is about 72% by weight and the crosslinked components are about 24% by weight of the first layer.

8. The multilayer thermoplastic film of claim 1 , wherein the first layer exhibits a permanent marker stain removal value of greater than about 90% light transmission.

9. The multilayer thermoplastic film of claim 1 , wherein the first layer exhibits a tar stain removal of between about 4.5 to 22 Delta YI.

10. The multilayer thermoplastic film of claim 1 , wherein the first layer exhibits a scratch resistance of greater than about 85 gloss units.

11. The multilayer thermoplastic film of claim 1 , wherein the first layer has a gloss of greater than about 90 gloss units.

12. The multilayer thermoplastic film of claim 1 , wherein the first layer is bonded to one major surface of the second layer.

13. The multilayer thermoplastic film of claim 12 , further comprising a pressure sensitive adhesive (PSA) layer bonded to an opposite major surface of the second layer such that the second layer is positioned between the first layer and the PSA layer.

14. A method for making a multilayer thermoplastic film comprising:

(a) combining a first thermoplastic polymer with crosslinked components and a photoinitiator to form a first layer comprising an interpenetrating network precursor, wherein the first thermoplastic polymer is a cured polymer selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof, and wherein the crosslinked components are selected from the group consisting of acrylates, methacrylates, and allylic isocyanurates,

(b) coextruding the interpenetrating network precursor with a second layer comprising a second thermoplastic polymer to form a multilayer thermoplastic film, wherein the second thermoplastic polymer is selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof, and

(c) curing the interpenetrating network precursor to form an interpenetrating network, wherein the multilayer thermoplastic film comprises an interpenetrating network layer and one or more layers of the second thermoplastic polymer, and wherein the interpenetrating network layer has a thickness of about 0.2 mil to about 3 mil.

15. A method for making a multilayer thermoplastic film comprising:

(a) combining a first thermoplastic polymer with crosslinked components and a photoinitiator to form an interpenetrating network precursor, wherein the first thermoplastic polymer is a cured polymer selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof, and wherein the crosslinked components are selected from the group consisting of acrylates, methacrylates, and allylic isocyanurates,

(b) extruding the interpenetrating network precursor to form a first layer;

(c) extruding a second thermoplastic polymer to form a second layer, wherein the second thermoplastic polymer is selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof;

(d) depositing the interpenetrating network precursor onto the second thermoplastic polymer; and

(e) curing the interpenetrating network precursor to form an interpenetrating network, and wherein the interpenetrating network layer has a thickness of about 0.2 mil to about 3 mil.

16. The method of claim 15 , wherein the multilayer thermoplastic film has a permanent marker stain removal value of greater than about 90%, a tar stain removal of between about 4.5 to 22 Delta YI, a scratch resistance of greater than about 85 gloss units, and a gloss of greater than about 90 gloss units.

17. The method of claim 15 , further comprising adding additives or stabilizers to the first thermoplastic polymer the crosslinked components, and the photoinitiator.

18. The method of claim 15 , wherein the interpenetrating network precursor is cured by e-beam, ultraviolet light, irradiation, or heat.

19. The method of claim 15 , wherein the crosslinked components are combined with the first thermoplastic polyurethane by mixing, compounding or imbibing.

20. A multilayer thermoplastic film comprising: a first layer comprising an interpenetrating network, wherein the interpenetrating network comprises:

a first thermoplastic polymer, wherein the first thermoplastic polymer is a cured polymer selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof,

crosslinked components, wherein the crosslinked components are selected from the group consisting of triallyl isocyanurate (TAIC), trimethylolpropane triacrylate (TMPTA), di-trimethylolpropane tetraacrylate (DTMPTA), and tri-functional methacrylate, and

a photoinitiator, wherein the crosslinked components and the photoinitiator are combined with the cured polymer to form the interpenetrating network; and

a second layer comprising one or more layers of a second thermoplastic polymer, wherein the second thermoplastic polymer is selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof.

21. A multilayer thermoplastic film comprising:

a first layer comprising an interpenetrating network, wherein the interpenetrating network comprises:

a first thermoplastic polymer, wherein the first thermoplastic polymer is a cured polymer selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof,

crosslinked components, wherein the crosslinked components are selected from the group consisting of acrylates, methacrylates, and allylic isocyanurates, and

a photoinitiator, wherein the photoinitiator is selected from the group consisting of 1-hydroxy-cyclohexyl-phenyl ketone, a mixture of oxy-phenyl-acetic acid 2-[2 oxo-2-acetoxy-ethoxy]-ethyl ester and oxy-phenyl-acetic 2-[2-hydroxy-ethoxy]-ethyl ester, phosphine oxide, phenylbis(2,4,6-trimethylbenzoyl) phosphine oxide, diphenyl (2,4,6-trimethylbenzoyl)-phosphine oxide (TPO), methylbenzoylformate (MBF), oligo[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone], 2,2-dimethoxy-1,2-diphenyl-ethanone (BDK), ethyl phenyl (2,4,6-trimethylbenzoyl) phosphinate, ethyl (2,4,6-trimethylbenzoyl)-phenyl-phosphinate, a mixture of 2 hydroxy-2-methylpropiophenone, ethyl (2,4,6-trimethylbenzoyl) (phenylphosphinate and oligo[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone]), difunctional alpha-hydroxy ketone, oligo(2-hydroxy-2-methyl-1-(4-(1-methylvinyl)phenyl)propanone), a blend of diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide and 2-hydroxy-2-methyl-1-phenyl-propanone, a blend of piparazino based aminoalkylphenone and pentaerythritol tetraacrylate (PPTTA), polyethylene glycol di(beta-4-[4-(2-dimethylamino-2-benzyl) butanoyl phenyl]piperazine)propionate, 2,3-dihydro-6-(2-hydroxy-2-methyl-1-oxopropyl)-1,1,3-trimethyl-3-[4-(2-hydroxy-2-methyl-1-oxopropyl)phenyl]-1H-indene; a mixture of 2,3-dihydro-5-(2-hydroxy-2-methyl-1-oxopropyl)-1,1,3-trimethyl-3-[4-(2-hydroxy-2-methyl-1-oxopropyl)phenyl]-1H-indene and 2-hydroxy-2-methylpropiophenone, 70% oligo[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone] mixed with 30% 2-hydroxy-2-methylpropiophenone, diester of carboxymethoxy-benzophenone and polytetramethyleneglycol 250, and a mixture of 1-propanone, 1,1′-(oxydi-4,1-phenylene)-bis(2-hydroxy-2-methyl and 1-hydroxycyclohexyl phenyl ketone) wherein the crosslinked components and the photoinitiator are combined with the cured polymer to form the interpenetrating network; and

a second layer comprising one or more layers of a second thermoplastic polymer, wherein the second thermoplastic polymer is selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof.

22. A multilayer thermoplastic film comprising:

a first layer comprising an interpenetrating network, wherein the interpenetrating network comprises:

a first thermoplastic polymer, wherein the first thermoplastic polymer is a cured polymer selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof,

crosslinked components, wherein the crosslinked components are selected from the group consisting of acrylates, methacrylates, and allylic isocyanurates, and

a photoinitiator, wherein the crosslinked components and the photoinitiator are combined with the cured polymer to form the interpenetrating network, wherein the first layer comprises about 65% to about 75% by weight of the first thermoplastic polymer and about 20% to about 30% by weight of the crosslinked components; and

a second layer comprising one or more layers of a second thermoplastic polymer, wherein the second thermoplastic polymer is selected from the group consisting of a polyurethane, polycarbonate, polycaprolactone, and a combination thereof.