Method for preparing polarizing plate locally having depolarization region, and polarizing plate prepared by using same
The present invention relates to a method for manufacturing a polarizing plate, the method including: preparing a polarizing plate where a protection film is laminated on one surface of a polyvinyl alcohol-based polarizer dyed with at least one or more of iodine and dichromatic dyes; and forming a depolarization region having single transmittance of 80% or more at a wavelength band in a range of 400 nm to 800 nm by bringing a decoloring solution including 1 to 30 wt % of a decolorant into local contact with the other surface of the polarizer, and a polarizing plate manufactured by using the same.
1. A polarizing plate comprising:
a polyvinyl alcohol-based polarizer dyed with at least one or more of iodine and dichromatic dyes, and
a protection film laminated on at least one surface of the polyvinyl alcohol-based polarizer,
wherein the polarizing plate locally has at least one depolarization region having single transmittance of 80% or more at a wavelength band in a range of 400 nm to 800 nm, and arithmetic mean roughness (Ra) of the depolarization region is 100 nm or less,
an area of at least one depolarization region is 0.5 mm 2 or more and 500 mm 2 or less, and
the depolarization region has a haze of 3% or less.
2. The polarizing plate of claim 1 , wherein root mean square roughness (Rq) of the depolarization region is 100 nm or less.
3. The polarizing plate of claim 1 , wherein in the depolarization region of the polarizing plate, a polarization degree is 20% or less.
4. The polarizing plate of claim 1 , wherein in a region of the polarizing plate other than the depolarization region, the single transmittance is 40% to 45% and a polarization degree is 99% or more.
5. The polarizing plate of claim 1 , wherein in the depolarization region, a content of at least one or more of the iodine and dichromatic dyes is 0.1 wt % to 0.5 wt %, and in a region other than the depolarization region, the content of at least one or more of the iodine and dichromatic dyes is 1 wt % to 4 wt %.