Aluminum alloys for applications such as wheels and methods of manufacture
Aluminum alloys described herein include silicon, iron, copper, manganese, magnesium, and chromium. In various implementations, the aluminum alloys also include one or more of zinc and titanium. Typically, a total amount of iron and manganese in the aluminum alloys is no less than 0.28% by weight and no greater than 0.45% by weight, and the grains in the aluminum alloys have an average grain length of no greater than 6 mm. Aluminum alloy billets can be forged for wheel production at selected temperatures.
1. An aluminum wheel having a rim and a disc, the aluminum wheel formed of an aluminum alloy comprising, by weight:
0.80% to 1.20% silicon;
0.08% to 0.37% iron;
0.35% to 0.55% copper;
0.08% to 0.37% manganese;
0.70% to 1.20% magnesium;
0.05% to 0.11% chromium;
no more than 0.20% zinc; and
no more than 0.05% titanium,
and the balance of weight percent comprising aluminum and incidental elements and impurities,
wherein the aluminum alloy has a total amount of iron and manganese no less than 0.28% by weight and no greater than 0.45% by weight;
wherein the disc includes aluminum alloy grains that have an average grain length that is no less than 0.4 millimeters (mm) and no greater than 6 mm.
2. The aluminum wheel according to claim 1 , wherein the total amount of iron and manganese is no less than 0.30% by weight and no greater than 0.37% by weight.
3. The aluminum wheel according to claim 1 , wherein the aluminum alloy grains have an average grain width that is no greater than 0.40 mm.
4. The aluminum wheel according to claim 1 , wherein the disc has a disc area, the disc area including less than 50% by area fraction of fine grains.
5. The aluminum wheel according to claim 1 , wherein a total amount of iron and manganese is no less than 0.28% by weight.
6. The aluminum wheel according to claim 1 , wherein the total amount of iron and manganese is no greater than 0.45% by weight.
7. The aluminum wheel according to claim 1 , wherein the total amount of iron and manganese is no less than 0.30% by weight and no greater than 0.37% by weight.
8. The aluminum wheel according to claim 1 , wherein the disc further comprises dispersoids, a dispersoid distribution in the aluminum alloy being no greater than 0.2 per μm 2 .
9. An aluminum wheel having a rim and a disc, the aluminum wheel formed of an aluminum alloy comprising, by weight:
0.80% to 1.20% silicon;
0.08% to 0.37% iron;
0.35% to 0.55% copper;
0.08% to 0.37% manganese;
0.70% to 1.20% magnesium;
0.05% to 0.11% chromium;
no more than 0.20% zinc; and
no more than 0.05% titanium,
and the balance of weight percent comprising aluminum and incidental elements and impurities,
wherein the aluminum alloy comprises a plurality of aluminum alloy grains, the plurality of aluminum alloy grains having an average grain length that is no less than 0.4 mm and no greater than 6 millimeters (mm).