Method of preparing lithium metal oxide and method of manufacturing lithium secondary battery
In a method of preparing a lithium metal oxide, a preliminary lithium metal oxide is prepared. The preliminary lithium metal oxide is washed using an organic washing solution to remove lithium salt impurities. The organic washing solution includes an organic solvent and a multivalent carboxylic acid compound. A minimum distance between oxygen atoms included in different carboxylic acid groups neighboring each other in the multivalent carboxylic acid compound is 220 pm or more.
1. A method of preparing a lithium metal oxide, the method comprising:
preparing a preliminary lithium metal oxide; and
washing the preliminary lithium metal oxide using an organic washing solution to remove lithium salt impurities, wherein the organic washing solution includes an organic solvent and a multivalent carboxylic acid compound, and a minimum distance between oxygen atoms included in different carboxylic acid groups neighboring each other in the multivalent carboxylic acid compound is equal to or greater than 220 pm; and
filtering the washed preliminary lithium metal oxide to remove the multivalent carboxylic acid compound capturing the lithium salt impurities from the washed preliminary lithium metal oxide.
2. The method according to claim 1 , wherein the minimum distance is in a range from 220 pm to about 500 pm.
3. The method according to claim 2 , wherein the lithium salt impurities include LiOH and Li 2 CO 3 .
4. The method according to claim 1 , wherein the multivalent carboxylic acid compound includes at least one selected from the group consisting of maleic acid, oxalic acid and poly acrylic acid (PAA).
5. The method according to claim 1 , wherein the organic solvent includes alcohol.
6. The method according to claim 1 , further comprising, before or after washing the preliminary lithium metal oxide using the organic washing solution, firing the preliminary lithium metal oxide.
7. The method according to claim 1 , wherein the lithium metal oxide includes a compound represented by Chemical Formula 1 below:
Li 1+α Ni 1−(x+y) Co x M y O 2 Chemical Formula 1
wherein −0.05≤α≤0.15, 0.01≤x≤0.2, 0≤y≤0.2, and M is at least one element selected from the group consisting of Mg, Sr, Ba, B, Al, Si, Mn, Ti, Zr, and W.
8. A method of manufacturing a lithium secondary battery, the method comprising:
preparing a cathode active material including the lithium metal oxide prepared according to claim 1 ;
coating the cathode active material on a cathode current collector to form a cathode; and
forming an anode facing the cathode with respect to a separation layer.