Carrier, catalyst, methods for producing them and method for producing ethylene oxide
View Patent ↗A carrier for an ethylene epoxidation catalyst, the carrier comprising a porous alumina body formed of sintered particles of alumina in a substantial absence of inorganic binder species other than alumina, wherein the substantial absence of inorganic binder species corresponds to an amount of less than 0.6 wt % inorganic binder species other than alumina and comprises at least a substantial absence of silicon-containing species.
1. A method for producing a carrier for an ethylene epoxidation catalyst in which the carrier comprises a porous alumina body formed of sintered particles of low soda alumina in a substantial absence of inorganic oxides other than alumina, the method comprising:
a) preparing a composition comprising low soda alumina particles, water, and a volatile organic binder, in the substantial absence of inorganic oxides other than alumina;
b) molding the composition into a structure;
c) heating the structure to volatilize the volatile organic binder and form a porous structure; and
d) sintering the porous structure at a temperature of 1350° C. or above to produce the porous alumina body formed of sintered particles of low soda alumina in a substantial absence of inorganic oxides other than alumina;
wherein the substantial absence of inorganic oxides corresponds to an amount of no more than 0.5 wt % inorganic oxides other than alumina and comprises at least a substantial absence of silicon-containing species.
2. The method of claim 1 , wherein the substantial absence of inorganic oxides corresponds to an amount of less than 0.1 wt % inorganic oxides other than alumina.
3. The method of claim 1 , wherein the substantial absence of inorganic oxides corresponds to an amount of 0.05 wt % or less inorganic oxides other than alumina.
4. The method of claim 1 , wherein the low soda alumina particles have an α-alumina composition in a substantial absence of other types of alumina.
5. The method of claim 1 , wherein the silicon-containing species are in an amount of less than 0.5 wt %.
6. The method of claim 1 , wherein, in the sintering, a sintering temperature is 1500° C. or more and 1650° C. or less.
7. The method of claim 1 , wherein in the sintering, a sintering time is 10 minutes or more and 10 hours or less.
8. The method of claim 1 , wherein the carrier has a B.E.T. surface area in a range of about 0.1 to 10 m 2 /g.
9. The method of claim 1 , wherein a pore size of 1-10 μm of the carrier contributes at least 50% of a total pore volume of the carrier, and a pore size of 5-10 μm of the carrier contributes at most 25% of the total pore volume of the carrier.