Catalyst for catalyzing formaldehyde oxidation and the preparation and use of the same
The present invention relates to a catalyst comprising manganese oxides wherein the manganese oxides comprise: MnO in an amount of 40-60 mole %, based on mole of Mn; Mn 2 O 3 in an amount of 40-60 mole %, based on mole of Mn; and Mn 3 O 4 in an amount of 1-10 mole %, based on mole of Mn. The present invention also relates to a method for preparing the catalysts and the use of the catalyst in an air purifier. The catalyst according to the present invention can effectively catalyze formaldehyde oxidation at ambient temperature so as to effectively remove indoor formaldehyde being present in relative low amounts.
1. A catalyst comprising manganese oxides wherein the manganese oxides comprise:
MnO in an amount of 40-60 mole %, based on mole of Mn;
Mn 2 O 3 in an amount of 40-60 mole %, based on mole of Mn; and
Mn 3 O 4 in an amount of 1-10 mole %, based on mole of Mn, and wherein the total mole of Mn in the catalyst is 100 mole %.
2. The catalyst as set forth in claim 1 , wherein the manganese oxides provide Mn 2+ and Mn 3+ in a mole ratio of (0.92-1.08):1.
3. The catalyst as set forth in claim 1 , further comprising a carrier.
4. The catalyst according to claim 3 , wherein the catalyst comprises 20-80 wt % of manganese oxides, 20-70 wt % carrier and 0-50 wt % adhesive.
5. The catalyst as set forth in claim 3 , wherein the carrier is selected from the group consisting of silica, alumina, active carbon, zeolite and molecular sieves.
6. The catalyst according to claim 3 , the catalyst further comprising an adhesive being selected from the group consisting of polyvinyl alcohol, cellulose polyurethane, epoxy and acrylates.
7. The catalyst according to claim 3 , the catalyst further comprising an adhesive being selected from the group consisting of carboxymethyl cellulose, carboxyethyl cellulose, methyl cellulose, hydroxymethyl cellulose, hydroxyethyl cellulose and hydroxypropyl cellulose.
8. A method for preparing the catalyst according to claim 3 , comprising the steps of:
preparing Mn 2 O 3 from MnCO 3 ;
preparing MnO from MnCO 3 ;
preparing Mn 3 O 4 from MnO;
preparing a slurry comprising Mn 2 O 3 , MnO, Mn 3 O 4 , a carrier and an adhesive; and
preparing the catalyst from the slurry.
9. The method according to claim 8 , wherein the step of preparing Mn 2 O 3 from MnCO 3 comprises the step of:
calcinating MnCO 3 at 673-873K for 2-6 hours in air.
10. The method according to claim 8 , wherein the step of preparing MnO from MnCO 3 comprises the steps of:
calcinating MnCO 3 at 673-873K for 3-6 hours under a hydrogen atmosphere, and
cooling to room temperature under a nitrogen atmosphere.
11. The method according to claim 8 , wherein the step of preparing Mn 3 O 4 from MnO comprises the steps of:
aging MnO at room temperature for 3-6 hours in air, and
further aging at 673-693K for 2-6 hours in air.
12. The method according to claim 8 , wherein the step of preparing the catalyst from the slurry comprises the steps of:
forming particles having a particle size of 2-3 mm from the slurry,
aging the particles for 2-4 hours, and
heating at 473-573K for 4-6 hours.
13. An air purifier, comprising the catalyst according to claim 1 .
14. The air purifier according to claim 13 , wherein the catalyst is arranged, as seen in the direction of air flow, after a particle filter, an electrostatic filter and/or an active carbon filter.