Directly printed panel having a two-layer design
A panel and a method for manufacturing of such a panel with a carrier plate, comprising a front side and a back side, and wherein the carrier plate comprises a layer system at least at the front side that is built from various polymer layers with different hardness values.
1. A panel comprising a carrier plate having a front side and a back side, wherein the carrier plate has a layer system at least at the front side, and the carrier plate comprises tongue and groove elements at its sides, enabling coupling of various similar panels in parallel direction to the front side and perpendicular to the front side by form fitting, wherein the layer system, originating of the front side, comprises:
a first elastic layer S 1 made of an polymer, having a thickness of 20 to 600 μm and a Martens hardness M S1 of 0.5 to 120 N/mm 2 ;
a second layer S 2 made of a polymer, having a thickness of 10 to 180 μm and a Martens hardness M S2 , wherein M S2 >M S1 ; and
a decor layer arranged between the front side and the layer S 1 , comprising a printing ink; the printing ink is based on a polymerizable acrylate and/or N-vinylcaprolactam.
2. The panel according to claim 1 , wherein the polymer of the layer S 1 is an aliphatic polymer.
3. The panel according to claim 1 , wherein M S1 is between 2 and 50 N/mm 2 .
4. The panel according to claim 1 , wherein M S2 is between 50 and 300 N/mm 2 .
5. The panel according to claim 1 , wherein the first elastic layer S 1 has a thickness of 40 to 500 μm.
6. The panel according to claim 1 , wherein the second elastic layer S 2 has a thickness of 10 to 180 μm.
7. The panel according to claim 1 , wherein the polymer of the layer S 1 is based on a radiation hardened aliphatic acrylate.
8. The panel according to claim 1 , wherein a third elastic layer S 3 is arranged between the front side and decor layer, having a Martens hardness M S3 , wherein M S3 ≤M S1 .
9. The panel according to claim 8 , wherein the layer S 3 has a thickness of 10 to 300 μm.
10. The panel according to claim 1 , wherein the printing ink of the decor layer and at least a part of the layer S 1 have been hardened together.
11. The panel according to claim 1 , wherein the decor layer has been applied by digital printing.
12. The panel according to claim 1 , wherein the polymer of the layer S 2 is based on one or more of the following acrylates: 1,6-hexandioldiacrylate, polyester acrylate, polyurethane acryl acid ester or dipropylene glycole diacrylate.
13. The panel according to claim 1 , wherein the carrier plate has a thickness between 3 and 20 mm.
14. The panel according to claim 1 , wherein the carrier plate is a MDF plate, a HDF plate, a PVC plate, a cement fiber plate, a WPC plate (wood powder composite), a thermoplastic recycling plate, wood plate, a wood veneer plate, or a parquet plate.
15. The panel according to claim 1 , wherein no paper or plastic foil is applied to the front side of the panel.
16. The panel according to claim 8 , wherein the source materials of the layers S 1 , S 2 , and S 3 are radiation hardenable materials.
17. The panel according to claim 1 , wherein the layers S 1 and S 2 are transparent.
18. The panel according to claim 1 , wherein the panel is not provided with abrasion-resistant particles.
19. The panel according to claim 1 , wherein the layer system has a damping effect of at least 5 dB, compared to the uncoated carrier plate, measured according to EPLF norm.
20. The panel according to claim 1 , wherein the hardness of the elastic layer S 1 is substantially constant over the total thickness, and in that the hardness differences within the layer are less than 20 N/mm 2 .
21. The panel according to claim 1 , wherein the panel is a wall panel, ceiling panel, or floor panel.
22. The panel according to claim 1 , wherein M S1 is between 2 and 40 N/mm 2 .
23. The panel according to claim 1 , wherein M S2 is between 15 and 150 N/mm 2 .
24. The panel according to claim 1 , wherein the first elastic layer S 1 has a thickness of 80 to 450 μm.
25. The panel according to claim 1 , wherein the second elastic layer S 2 has a thickness of 20 to 100 μm.
26. The panel according to claim 1 , wherein the polymer of the layer S 1 is based on a radiation hardened aliphatic urethane acrylate.
27. The panel according to claim 1 , wherein the printing ink of the decor layer and at least a part of the layer S 1 have been hardened together by radiation.