Electrolytic copper foil and secondary battery using the same
The present disclosure provides an electrolytic copper foil composed of a single layer or a stack of two or more layers, wherein the electrolytic copper foil has Total Organic Carbon (TOC) content equal to or smaller than 4 ppm, and has chlorine (Cl) content equal to or smaller than 10 ppm, wherein the electrolytic copper foil has a thickness, a tensile strength, and an elongation satisfying a relationship 1 below: relationship 1: thickness (μm)/(tensile strength (kgf/mm 2 )*elongation (%))≤0.1.
1. An electrolytic copper foil composed of a single layer or a stack of two or more layers, wherein the electrolytic copper foil has Total Organic Carbon (TOC) content of 0.5 to 3 ppm, and has chlorine (Cl) content of 0.1 to 4 ppm, wherein the electrolytic copper foil has a thickness, a tensile strength, and an elongation satisfying a relationship 1 below, and wherein a breakage height obtained by an Erichsen test when the thickness of the electrolytic copper foil during the Erichsen test is 35 μm or larger is 3 mm or larger, wherein a gloss (Gs(60°)) of the copper foil is equal to or greater than 100:
thickness(μm)/(tensile strength(kgf/mm 2 )* elongation(%))≤0.1, relationship 1
wherein the tensile strength of the electrolytic copper foil is 45 to 96.6 kgf/mm 2 , and the elongation of the copper foil is 3 to 11%.
2. An anode for a lithium secondary battery, wherein the anode includes an anode current collector, wherein the electrolytic copper foil of claim 1 is used as the anode current collector such that an anode active material is coated on the electrolytic copper foil at a loading level of 1.0 g/cm 3 or greater.
3. A lithium secondary battery including a battery housing, an electrode assembly and an electrolytic solution, wherein the electrode assembly and electrolytic solution are accommodated in the battery housing,
wherein the electrode assembly includes:
an anode, wherein the anode includes an anode current collector, wherein the electrolytic copper foil of claim 1 is used as the anode current collector, wherein the anode includes an anode active material coated on the electrolytic copper foil;
a cathode electrically connected to the anode and coated with a cathode active material containing a lithium compound; and
a separator interposed between the anode and the cathode.
4. A printed circuit board having, on one face thereof, the electrolytic copper foil of claim 1 .
5. An anode for a lithium secondary battery, wherein the anode includes an anode current collector, wherein the electrolytic copper foil of claim 1 is used as the anode current collector such that an anode active material is coated on the electrolytic copper foil at a loading level of 1.0 g/cm 3 or greater.
6. A lithium secondary battery including a battery housing, an electrode assembly and an electrolytic solution, wherein the electrode assembly and electrolytic solution are accommodated in the battery housing,
wherein the electrode assembly includes:
an anode, wherein the anode includes an anode current collector, wherein the electrolytic copper foil of claim 1 is used as the anode current collector, wherein the anode includes an anode active material coated on the electrolytic copper foil;
a cathode electrically connected to the anode and coated with a cathode active material containing a lithium compound; and
a separator interposed between the anode and the cathode.
7. A printed circuit board having, on one face thereof, the electrolytic copper foil of claim 1 .
8. The electrolytic copper foil according to claim 1 , wherein the electrolytic copper foil consists essentially of Total Organic Carbon (TOC) content of 0.5 to 3 ppm and chlorine (Cl) content of 0.1 to 4 ppm.
9. The electrolytic copper foil according to claim 8 , wherein the electrolytic copper foil consists of Total Organic Carbon (TOC) content of 0.5 to 3 ppm and chlorine (Cl) content of 0.1 to 4 ppm.