USE OF AN EPOXY RESIN COMPOSITION AND POWER PRODUCT WITH EPOXY RESIN COMPOSITION
An epoxy resin composition in an outdoor application and/or a high voltage application of an electrical insulation is described. The epoxy resin composition includes an aliphatic epoxy resin; and a catalyst system. The catalyst system is present in a content of 0.5-5 phr in the epoxy composition. The catalyst system includes at least one of the group consisting of: BX amine complex and blocked super acid. The epoxy resin composition is substantially anhydride-free. Further, a power product including insulation is described. The insulation includes a hydrophobic, cycloaliphatic epoxy resin; and a catalyst system. The catalyst system is present in a content of 0.5-5 phr in the epoxy composition. The catalyst system includes at least one of the group consisting of: BX amine complex and blocked super acid. The epoxy resin composition is substantially anhydride-free.
1 . A combination, comprising:
an epoxy resin composition in an outdoor application of an electrical insulation, the epoxy resin composition comprising:
an aliphatic epoxy resin;
a catalyst system, wherein the catalyst system is present in a content of 0.5-5 phr in the epoxy composition;
the catalyst system comprising at least one of the group consisting of: BX 3 amine complex and blocked super acid, the “X” in BX 3 standing for a halogenide;
wherein the epoxy resin composition is anhydride-free.
2 . A combination, comprising:
an epoxy resin composition in a medium and high voltage application of an electrical insulation, the epoxy resin composition comprising:
an aliphatic epoxy resin;
a catalyst system, wherein the catalyst system is present in a content of 0.5-5 phr in the epoxy composition and comprises a blocked super acid;
wherein the epoxy resin composition is anhydride-free.
3 . The combination according to claim 1 , wherein the BX 3 amine complex is a N,N-dimethyl-octyl amino complex of boron trichloride or derivatives of a N,N-dimethyl-octyl amino complex of boron trichloride.
4 . The combination according to claim 1 , wherein the blocked super acid is chosen from the group of hexafluoroantimonate, derivatives of hexafluoroantimonate and complexes of hexafluoroantimonate.
5 . The combination according to claim 1 , wherein the catalyst system includes both a BX 3 amine complex and a blocked super acid.
6 . The combination according to claim 1 , wherein the content of the BX 3 amine complex in the composition is between 1.5 and 3 phr.
7 . The combination according to claim 1 , wherein the resin is a hydrophobic resin.
8 . The combination according to claim 1 , wherein the aliphatic resin is a cycloaliphatic resin.
9 . The combination according to claim 1 , wherein the aliphatic epoxy resin is based on a diglycidyl ester of hexahydrophthalic acid.
10 . The combination according to claim 1 , wherein the epoxy resin composition is a homopolymerized epoxy resin composition.
11 . The combination according to claim 1 , wherein the outdoor applications comprises utilization in a temperature range not below −40° C. and not above +70° C., a humidity up to 100%, a UV index up to 11, and/or a salinity of the ambient air up to 200000 microSiemens/cm.
12 . The combination according to claim 1 , wherein the epoxy resin composition comprises the application in at least one of: in medium and/or high-voltage insulations for outdoor environments, support insulators, current and voltage transformers and sensors, bushings, as impregnating resins, for outdoor insulators associated with high-voltage lines, in long-rods, in composite and cap-type insulators, in base insulators, in the production of insulators associated with outdoor power switches, in measuring transducers, in lead-throughs, in overvoltage protectors, in switchgear constructions, in power switches, dry-type transformers and electrical machines, in coating materials for transistors and other semiconductor elements.
13 . The combination according to claim 1 , wherein the epoxy resin composition passes the inclined tracking and erosion test according to standard IEC 60587, class 1A3.5 at 3.5 Kv AND 4.5 Kv.
14 . The combination of according to claim 1 , wherein the epoxy resin composition withstands temperatures minimum −40° C. without cracking.
15 . A power product for outdoor applications comprising an electrical insulation with a homopolymerized epoxy resin composition, comprising:
a hydrophobic, cycloaliphatic resin;
a catalyst system, wherein the catalyst system is present in a content of 0.5-5 phr in the epoxy composition;
the catalyst system comprising at least one of the group consisting of: BX 3 amine complex and blocked super acid, the “X” in BX 3 standing for a halogenide;
wherein the epoxy resin composition is anhydride-free.
16 . The combination according to claim 2 , wherein the BX 3 amine complex is a N,N-dimethyl-octyl amino complex of boron trichloride or derivatives of a N,N-dimethyl-octyl amino complex of boron trichloride.
17 . The combination according to claim 2 , wherein the blocked super acid is chosen from the group of hexafluoroantimonate, derivatives of hexafluoroantimonate and complexes of hexafluoroantimonate.
18 . The combination according to claim 2 , wherein the catalyst system includes both a BX 3 amine complex and a blocked super acid.
19 . The combination according to claim 2 , wherein the content of the BX 3 amine complex in the composition is between 1.5 and 3 phr.
20 . The combination according to claim 2 , wherein the resin is a hydrophobic resin.