Method of preparing lithium metal oxide and method of manufacturing lithium secondary battery
In a method of preparing a lithium metal oxide, a preliminary lithium metal oxide is prepared. The preliminary lithium metal oxide is washed using a washing solution to remove lithium salt impurities. The washing solution includes water and an organic ligand multimer compound. The lithium metal oxide having improved structural uniformity and stability is obtained using the washing solution.
1. A method of preparing a lithium metal oxide, comprising:
preparing a preliminary lithium metal oxide; and
washing the preliminary lithium metal oxide using a washing solution to remove lithium salt impurities, the washing solution including water and an organic ligand multimer compound
wherein the organic ligand multimer compound includes at least one element having at least one unshared electron pair.
2. The method according to claim 1 , wherein the element having the unshared electron pair forms a coordination bond or an ionic bond with lithium or a metal element except for lithium of the preliminary lithium metal oxide.
3. The method according to claim 1 , wherein the organic ligand multimer compound includes at least two different elements having the unshared electron pair.
4. The method according to claim 3 , wherein the organic ligand multimer compound includes sulfur (S) and oxygen (O), or includes sulfur (S) and nitrogen (N).
5. The method according to claim 1 , wherein the organic ligand multimer compound includes at least one of a heteroaryl group or a heteroallyl group.
6. The method according to claim 1 , wherein an amount of the organic ligand multimer compound is in a range from 0.05 part by weight to 2.5 parts by weight based on 1 part by weight of LiOH in the lithium salt impurities.
7. The method according to claim 1 , wherein a remaining amount of the organic ligand multimer compound is in a range from 0.0005 wt % to 0.5 wt % based on a weight of the lithium metal oxide.
8. The method according to claim 1 , wherein the lithium metal oxide is represented by Chemical Formula 1:
Li 1+a Ni 1−(x+y) Co x M y O 2 [Chemical Formula 1]
wherein, in Chemical Formula 1, −0.05≤a≤0.15, 0.01≤x≤0.2, 0≤y≤0.2, and
M is at least one selected from Mg, Sr, Ba, B, Al, Si, Mn, Ti, Zr or W.
9. The method according to claim 8 , wherein the lithium metal oxide includes a metal oxide coating formed on at least a portion of a surface thereof.
10. A method of manufacturing a lithium secondary battery, comprising:
forming a cathode active material including the lithium metal oxide prepared according to claim 1 ;
coating the cathode active material on a cathode current collector to from a cathode; and
forming an anode facing the cathode with respect to a separation layer.