Reduction at elevated temperature of coated steels containing metastable austenite
Warming a metastable steel after coating and before or during cold rolling suppresses the transformation of austenite to martensite, resulting in lower mill loads and higher amounts of reduction at similar loads. As-warm rolled steel has enhanced mechanical properties when compared to steel reduced the same amount by cold rolling at room temperature.
1. A method of coating a metastable steel comprising the steps of:
a. Selecting a metastable steel having an instability factor (IF) greater than or equal to 2.9, wherein IF is calculated by the following equation:
IF=37.193−51.248(% C)−0.4677(% Cr)−1.0174(% Mn)−34.396(% N)−2.5884(% Ni)
b. Prior to coating said metastable steel, annealing said metastable steel;
c. Coating said metastable steel with a metallic coating;
d. After coating said metastable steel, warming said metastable steel to a warming temperature greater than 70° F.; and
e. Rolling said coated and warmed metastable steel.
2. The method of claim 1 , wherein the warming temperature is near or above the Md temperature for the particular metastable steel composition.
3. The method of claim 1 , wherein the warming temperature is near or above the Md30
temperature for the particular metastable steel composition.
4. The method of claim 1 , wherein the warming temperature is less than or equal to 930° F.
5. The method of claim 3 , wherein the Md30 temperature for the metastable steel is calculated according to the following equation:
Md 30=551−462(% C+% N)−68*% Cb−13.7*Cr−29(% Cu+% Ni)−8.1*% Mn−18.5*% Mo−9.2*% Si.
6. The method of claim 3 , wherein the Md30 temperature for the metastable steel is calculated according to the following equation:
Md 30=413−462*(% C+% N)−13.7*% Cr−8.1*% Mn−18.5*% Mo−9.5*% Ni−9.2*% Si.
7. The method of claim 1 , 2 , 3 , 4 , 5 , or 6 , further comprising the step of wherein after rolling, the metastable steel is further rolled at room temperature.
8. The method of claim 7 , further comprising the step of wherein the metastable coated steel is annealed prior to being rolled at room temperature.
9. The method of claim 1 , wherein the metallic coating comprises zinc, aluminum, or an alloy of one or more of them.