Method for manufacturing a light extraction structure for a UV lamp

1. A method for forming a light extraction layer comprising nanostructures, the method comprising:

providing a substrate, the substrate being at least partially transparent to ultraviolet (“UV”) light;

forming a non-aqueous precursor solution comprising fluorine, a solvent, and an alkaline earth metal to form alkaline earth metal difluoride particles, wherein the non-aqueous precursor solution is formed in a two-step sol-gel process by first forming a gel, followed by providing the solvent to the gel;

applying the non-aqueous precursor solution on at least a first side of the substrate;

drying the substrate at a first temperature for a first period of time; and

baking the substrate at a second temperature, higher than the first temperature, for a second period of time, to form a light extraction layer comprising alkaline earth metal difluoride nanostructures on the substrate.

2. The method according to claim 1 , wherein the nanostructures are nanograins.

3. The method according to claim 1 , wherein the first temperature is in the range of 50 to 150° C. and the first period of time is in the range of 10 s to 5 min.

4. The method according to claim 1 , wherein the second temperature is in the range of 200 to 400° C. and the second period of time is in the range of 1 min to 1 h.

5. The method according to claim 1 , wherein forming the non-aqueous precursor solution comprises:

forming a mixture comprising the solvent and an alkaline earth metal;

boiling the mixture with reflux forming a gel;

evaporating the solvent of the gel;

cooling down the gel;

adding the solvent to the gel;

heating the solvent with gel;

when the boiling point of the solvent with gel is reached, adding a compound comprising fluorine; and

boiling the gel such that a transparent sol comprising alkaline earth metal difluoride particles is formed.

6. The method according to claim 5 , wherein the step of boiling with reflux is performed for a time period in the range of 5 min to 1 h.

7. The method according to claim 5 , wherein the compound comprising fluorine is Trifluoroacetic acid, CF 3 CO 2 H.

8. The method according to claim 1 , wherein the nanostructures comprises at least one of MgF 2 , CaF 2 , BaF 2 and SrF 2 .

9. The method according to claim 1 , wherein applying the non-aqueous precursor solution on the substrate comprises, dip coating, spray coating or spin coating.

10. The method according to claim 1 , wherein the substrate is a tubular structure, and wherein applying the treated non-aqueous precursor solution to the substrate comprises dip coating of the tubular structure to form a light extraction layer on the inside and outside of the tubular structure.

11. The method according to claim 1 , wherein applying the non-aqueous precursor solution comprises applying a plurality of light extraction layers on the substrate.

12. The method according to claim 1 , wherein a size of the nanostructures is in the range of 1 to 200 nm.

13. The method according to claim 1 , wherein an average separation distance between nanostructures is in the range of 1 nm to 100 nm.

14. The method according to claim 1 , wherein the plurality of nanostructures are grains arranged in a polycrystalline layer.

15. The method according to claim 1 , wherein the plurality of nanostructures are at least partly transparent to the UV light.

16. The method according to claim 1 , wherein the substrate comprises at least one of borosilicate glass, soda-lime glass, sapphire, MgF 2 , and quartz.

17. A light extraction structure comprising a light extraction layer formed by the method according to claim 1 , the light extraction structure comprising:

a substrate at least partly transparent to UV light, the substrate having a first and a second side, the first side of the substrate arranged to face the UV light source and to receive UV light emitted by the UV light source; and

a light extraction layer arranged on at least one of the first and the second side of the substrate, the light extraction layer being configured to reduce an amount of UV light reflected by the substrate.

18. A UV lamp, comprising:

a UV light source, and

a light extraction structure according to claim 17 .

19. The UV lamp according to claim 18 , wherein the light extraction structure is arranged as an envelope of the UV light source.

20. The UV lamp according to claim 18 , further comprising a second light extraction structure arranged to enclose the first light extraction structure.

21. A method for forming a light extraction layer comprising nanostructures, the method comprising:

providing a substrate, the substrate being at least partially transparent to ultraviolet (“UV”) light;

forming a non-aqueous precursor solution comprising fluorine and an alkaline earth metal to form alkaline earth metal difluoride particles, wherein forming the non-aqueous precursor solution comprises:

forming a mixture comprising a solvent and an alkaline earth metal;

boiling the mixture with reflux forming a gel,

evaporating the solvent of the gel,

cooling down the gel,

adding the solvent to the gel,

heating the solvent with gel,

when the boiling point of the solvent with gel is reached, adding a compound comprising fluorine, and

boiling the gel such that a transparent sol comprising alkaline earth metal difluoride particles is formed;

applying the non-aqueous precursor solution on at least a first side of the substrate;

drying the substrate at a first temperature for a first period of time; and

baking the substrate at a second temperature, higher than the first temperature, for a second period of time, to form a light extraction layer comprising alkaline earth metal difluoride nanostructures on the substrate.