Foamable ethylene polymer
The invention relates to a foamable ethylene polymer composition comprising at least one antioxidant, at least one process aid and at least 80 wt % of a peroxide-treated ethylene polymer composition. The foamable ethylene polymer composition has melt strength of at least 2 cN, a density of 940 to 970 kg/m3, and dissipation factor measured at 1.9 GHz of 50-80−10 −6 . The invention further relates to a process for making such a foamable ethylene polymer composition, and use of the foamable ethylene polymer composition in a foamed cable insulation.
1. A foamable ethylene polymer composition, wherein said foamable ethylene polymer composition comprises
a. at least one antioxidant,
b. at least one process aid,
c. at least 80 wt % of a peroxide-treated ethylene polymer composition,
wherein said foamable ethylene polymer composition has a melt strength of at least 2 cN, a density of 940 to 970 kg/m 3 , and dissipation factor measured at 1.9 GHz of 50-80·10 −6 , and
wherein the amount of peroxide with which said peroxide-treated ethylene polymer composition was treated is 0.1 to 2 wt %.
2. The foamable ethylene polymer composition according to claim 1 , wherein said foamable ethylene polymer composition has MFR 2 (2.16 kg, 190° C.) of 0.1 to 10 g/10 min.
3. The foamable ethylene polymer composition according to claim 1 , wherein said foamable ethylene polymer composition has crystallinity of 70 to 90%.
4. The foamable ethylene polymer composition according to claim 1 , wherein said foamable ethylene polymer composition has crystallisation temperature of 110 to 130° C.
5. The foamable ethylene polymer composition according to claim 1 , wherein the process aid is a stearate.
6. The foamable ethylene polymer composition according to claim 1 , wherein said peroxide-treated ethylene polymer composition is derived from an ethylene polymer with a density of 940 to 970 kg/m 3 and an MFR 2 of 3 to 50 g/10 min prior to peroxide treatment.
7. The foamable ethylene polymer composition according to claim 1 , wherein said peroxide-treated ethylene polymer composition is derived from an ethylene polymer with a density of 950 to 970 kg/m 3 and an MFR 2 of 5 to 20 g/10 min prior to peroxide treatment.
8. The foamable ethylene polymer composition according to claim 1 , wherein the peroxide with which said peroxide-treated ethylene polymer composition is treated has a half-life temperature T½ at 0.1 h above 133° C.
9. The foamable ethylene polymer composition of claim 1 , wherein the at least one antioxidant comprises a phenolic antioxidant.
10. The foamable ethylene polymer composition of claim 9 , wherein the phenolic antioxidant is sterically hindered.
11. The foamable ethylene polymer composition of claim 9 , wherein the phenolic antioxidant is pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate).
12. The foamable ethylene polymer composition of claim 5 , wherein the stearate is zinc stearate.
13. The foamable ethylene polymer composition of claim 1 , wherein the melt strength is in the range of 3 cN to 15 cN and the density is in the range of 950 kg/m 3 to 970 kg/m 3 .
14. The foamable ethylene polymer composition of claim 1 , wherein the melt strength is in the range of 4 cN to 15 cN and the density is in the range of 960 kg/m 3 to 970 kg/m 3 .