Sliding member for vehicular suspension and method for producing same
View Patent ↗A sliding member for vehicular suspension includes a wear resistant layer having appropriate mechanical strength and high designability on its outer peripheral sliding face and a method for producing the same. On an outer peripheral sliding face of the sliding member for vehicular suspension, a colored wear resistant layer formed by an ion plating method and having a film thickness of 0.75 μm or more and 10 μm or less is included; and in the wear resistant layer, a dark blue titanium oxide layer, a titanium intermediate layer, and a colored titanium oxide layer are laminated in this order from the inner peripheral side toward the outer peripheral side.
1. A sliding member for vehicular suspension comprising;
a colored wear resistant layer formed by an ion plating method and having a film thickness of 0.75 μm or more and 10 μm or less, said wear resistant layer being provided on an outer peripheral sliding face of the sliding member, wherein
the wear resistant layer includes a dark blue titanium oxide layer, a titanium intermediate layer, and a colored titanium oxide layer, which are laminated in this order from an inner peripheral side toward an outer peripheral side of the sliding member, and
the colored titanium oxide layer has a color tone that is different from dark blue.
2. The sliding member for vehicular suspension according to claim 1 , wherein the colored titanium oxide layer is a bluish green titanium oxide layer having a film thickness of 0.15 μm or more and 0.19 μm or less.
3. A method for producing the sliding member for vehicular suspension according to claim 1 , wherein
the ion plating method comprises using a hollow cathode discharge (HCD) ion plating apparatus, setting a beam output of the apparatus on forming the colored titanium oxide layer to 180 to 280 A, and controlling an oxygen partial pressure within a vacuum tank of the apparatus to a range of 8.1×10 −2 Pa or more and 1.2×10 −1 Pa or less.
4. The method for producing the sliding member for vehicular suspension according to claim 3 , wherein the colored titanium oxide layer is a bluish green titanium oxide layer having a film thickness of 0.15 μm or more and 0.19 μm or less.
5. The sliding member for vehicular suspension according to claim 1 , wherein the colored titanium oxide layer has a film thickness between 0.05 μm and 0.3 μm.
6. The sliding member for vehicular suspension according to claim 1 , wherein the colored titanium oxide layer has the color tone selected from the group consisting of: bright yellow, bluish purple, yellow, reddish purple, bluish green, green, and yellowish green.
7. The sliding member for vehicular suspension according to claim 1 , wherein the colored titanium oxide layer is formed by the ion plating method where a beam output is in a range of 180 A and 280 A.