Friction material
The invention provides a friction material and a method of making the friction material. The friction material comprises man-made vitreous fibres whose chemical composition comprises: less than 2 wt % Fe 2 O 3 ; 30-40 wt % MgO+CaO; 35-45 wt % SiO 2 ; 17-24 wt % Al 2 O 3 ; and 1-5 wt % K 2 O+Na 2 O.
1. A friction material comprising man-made vitreous fibres (MMVF) dispersed in a matrix, the MMVF comprising:
less than 2 wt % Fe 2 O 3
30-40 wt % MgO+CaO
35-45 wt % SiO 2
17-24 wt % Al 2 O 3
1-5 wt % K 2 O+Na 2 O,
wherein the MMVF have a number mean diameter of from 3 to 5 μm,
wherein the MMVF are present in an amount of from 3 to 15 vol %.
2. The friction material of claim 1 , wherein the MMVF have a number mean diameter of from 3.5 to 4.5 μm.
3. The friction material of claim 1 , wherein the MMVF have a number mean length of from 100 to 600 μm.
4. The friction material of claim 1 , wherein the MMVF comprises:
less than 1.5 wt % Fe 2 O 3
34-39 wt % MgO+CaO
37-43 wt % SiO 2
18-23 wt % Al 2 O 3
2-4 wt % K 2 O+Na 2 O.
5. The friction material of claim 1 , wherein the matrix is a non-asbestos, copper-free matrix.
6. The friction material of claim 1 , wherein the matrix comprises no greater than 20 wt % steel fibres.
7. The friction material of claim 1 , wherein the matrix comprises a lubricant, an abrasive, a binder and a filler.
8. The friction material of claim 1 , wherein the friction material comprises from 5 to 17 vol % abrasives, from 0 to 10 vol % non-MMVF reinforcing fibres, from 5 to 17 vol % lubricants and from 5 to 25 vol % binder.
9. The friction material of claim 1 , wherein the binder comprises an organic thermosetting resin.
10. The friction material of claim 1 , wherein the matrix is free from electrically conductive polymer.
11. A method of making the friction material of claim 1 , the method comprising:
mixing MMVF and matrix raw materials to form a mixture; wherein the MMVF comprises less than 2 wt % Fe 2 O 3 , 30-40 wt % MgO+CaO, 35-45 wt % SiO 2 , 17-24 wt % Al 2 O 3 , 1-5 wt % K 2 O+Na 2 O; and wherein the MMVF have a number mean diameter of from 3 to 5 μm;
subjecting the mixture to above-ambient pressure to form a compact; and
heating the compact to form the friction material, wherein the MMVF are present in an amount of from 3 to 15 vol %.
12. The method of claim 11 , wherein the step of mixing MMVF and raw material to form a mixture comprises the sub-steps:
mixing the MMVF with a filler and any other fibres; and
adding in remaining components and mixing to form the mixture.
13. The method of claim 11 wherein the matrix raw materials comprises binder raw materials that are curable during the heating step and wherein the matrix raw materials are cured in the heating step.
14. The method of claim 11 , wherein the MMVF comprises no more than 0.5 wt % shot of size >125 μm.
15. The method of claim 11 , wherein the MMVF comprises no more than 1.5 wt % shot of size >63 μm.