Preform, its method of preparation and its use
The present invention relates to a composite preform comprising a multistage polymer. The present invention further relates to a method for making a composite preform comprising a fibrous material and a multistage polymer and its use in making composite articles. The present invention also relates to a process for preparing a composite preform comprising a fibrous material and a multistage polymer and its use for producing fibre reinforced impact modified composites.
1. A stable, pre-shaped, unfinished preform comprising:
a) a fibrous substrate and
b) a multi stage core shell polymer having at least two stages that are different from each other in polymer composition, and
c) which does not include a matrix of polymerizable continuous phase impregnating resin,
wherein the quantity of multi stage polymer is between 5 wt % and 30 wt % of the preform, and wherein the pre-shaped, unfinished preform is stable such that it has a fixed shape in the absence of said matrix of polymerizable continuous phase impregnating resin in the preform.
2. The stable, pre-shaped, unfinished preform according to claim 1 wherein the quantity of said multi stage core shell polymer is between 6 wt % and 25 wt %.
3. The stable, pre-shaped, unfinished preform according to claim 1 wherein the quantity of said multi stage core shell polymer is at least 7 wt %, based on the sum of the two compounds a) and b).
4. The stable, pre-shaped, unfinished preform according to claim 1 wherein the quantity of said multi stage core shell polymer is between 7 wt % and 25 wt %, based on the sum of the two compounds a) and b).
5. The stable, pre-shaped, unfinished preform according to claim 1 wherein the multistage core shell polymer is in form of spherical polymer particles having a weight average particle size between 20 nm and 800 nm.
6. The stable, pre-shaped, unfinished preform according to claim 1 wherein the multi stage core shell polymer comprises,
a) one stage (A) comprising a polymer (A1) having a glass transition temperature of less then 0° C., and
b), one stage (B) comprising a polymer (B1) having a glass transition temperature of at least 30° C.
7. The stable, pre-shaped, unfinished preform according to claim 6 wherein the polymers (A1) and (B1) are acrylic or methacrylic polymers.
8. The stable, pre-shaped, unfinished preform according to claim 6 wherein the polymer (A1) is a silicone rubber based polymer.
9. The stable, pre-shaped, unfinished preform according to claim 6 wherein the polymers (A1) comprises at least 50 wt % of polymeric units coming from isoprene or butadiene.
10. The stable, pre-shaped, unfinished preform according to claim 6 wherein stage (A) is the first stage and stage (B) comprising polymer (B1) is grafted on stage (A) comprising polymer (A1).
11. The stable, pre-shaped, unfinished preform according to claim 1 wherein the fibrous substrate comprises fibers having an aspect ratio of at least 1000.
12. The stable, pre-shaped, unfinished preform according to claim 1 wherein the fibrous substrate is chosen from the group consisting of stacked or folded fibrous mats, non-woven reinforcements, bundles of fibers, and mixtures thereof.
13. A process for manufacturing the stable, pre-shaped, unfinished preform according to claim 1 , said process comprising the steps of:
a) bringing into contact the fibrous substrate and an aqueous dispersion of the multistage core shell polymer,
b) drying the product of step a), and
c) heating the dried product of b) in a mold at a temperature between 100° C. and 250° C.
14. The process according to claim 13 wherein step b) is made by heating to at least 45° C.
15. The process according to claim 13 wherein step c) is made in a mold at a temperature between 100° C. and 250° C.