Composition comprising a multistage polymer and two different (meth)acrylic polymers, its method of preparation and article comprising it
The present invention relates to a composition comprising two different (meth)acrylic polymers and a multistage polymer. In particular the present invention it relates to polymeric composition comprising two different (meth)acrylic polymers and a multistage polymer. The invention also relates to a process for manufacturing such polymeric composition. More particularly the present invention relates also to a process for preparing an impact modified composition comprising two different (meth)acrylic polymers and a multistage polymer.
1. A polymeric composition comprising
A. a (meth)acrylic polymer (P1), wherein said (meth)acrylic polymer (P1) comprises at least 50 wt % monomers chosen from C1 to C12 alkyl (meth)acrylates,
B. a multistage, core-shell polymer and
C. a (meth)acrylic polymer (P2), which is different from the (meth)acrylic polymer (P1), in either the mass average molecular weight, the composition of the polymer, or both, and wherein the (meth)acrylic polymer (P2) has a mass average molecular weight Mw above 50,000 g/mol,
wherein the (meth)acrylic polymer (P1) has a mass average molecular weight Mw of less than 100,000 g/mol as measured by mass average molecular weight (Mw) of the polymers is measured with by size exclusion chromatography (SEC), and wherein the multi stage polymer comprises
a) one stage (A) comprising a polymer (A1) having a glass transition temperature of less than 0° C., and
b) one stage (B) comprising a polymer (B1) having a glass transition temperature of at least 30° C.
2. The composition according to claim 1 , wherein the (meth) acrylic polymer (P1) has a mass average molecular weight Mw between 5000 g/mol and 70,000 g/mol.
3. The composition according to claim 1 , wherein the (meth)acrylic polymer (P2) has a mass average molecular weight Mw higher than that of the (meth)acrylic polymer (P1).
4. The composition according to claim 1 , wherein the (meth)acrylic polymer (P2) has a mass average molecular weight Mw between 105,000 g/mol and 10,000,000 g/mol.
5. The composition according to claim 1 , wherein the (meth)acrylic polymer (P2) is crosslinked.
6. The composition according to claim 1 , wherein the the glass transition temperature Tg of the (meth)acrylic polymer (P2) is between 60° C. and 150° C. as measured by thermo mechanical analysis.
7. The composition according to claim 1 , wherein the (meth)acrylic polymer (P2) comprises at least 50 wt % of polymerized methyl methacrylate.
8. The composition according to claim 1 , wherein the stage (A) is the first stage and that stage (B) comprising polymer (B1) is grafted on stage (A) comprising polymer (A1).
9. The composition according to claim 1 , wherein the polymers (A1) and (B1) are acrylic or methacrylic polymers.
10. The composition according to claim 1 , wherein the polymer (A1) comprises at least 50 wt % of polymeric units coming from isoprene or butadiene.
11. The composition according to claim 1 , wherein the (meth) acrylic polymer (P1) comprises at least 50 wt % monomers selected from the group comprising C1 to C12 alkyl (meth)acrylates.
12. The composition according to claim 1 , wherein the (meth) acrylic polymer (P1) comprises from 50 wt % to 100 wt % methyl methacrylate, and from 0.2 wt % to 20 wt % of at least one C1 to C8 alkyl acrylate monomer.
13. The composition according to claim 1 , wherein the (meth) acrylic polymer (P1) comprises between 0 wt % and 50 wt % of a functional comonomer, wherein said comonomer has the formula (1) or (2):
wherein in both formulas (1) and (2) R 1 is chosen from H or CH 3 ; and in formula (1) Y is O, R 5 is H or an aliphatic or aromatic radical having at least one atom that is not C or H; and in formula (2) Y is N and R 4 and/or R 3 is H or an aliphatic or aromatic radical.
14. The composition according to claim 13 , wherein the (meth)acrylic polymer (P1) comprises between 1 wt % and 30 wt % of a functional monomer.
15. The composition according to claim 13 , wherein the functional comonomer is selected from the group consisting of glycidyl (meth)acrylate, acrylic acid, methacrylic acid, the amides derived from acrylic and methacrylic acid dimethylacrylamide, 2-methoxyethyl acrylate, 2-methoxyethyl methacrylate, 2-aminoethyl acrylates optionally quaternized, 2-aminoethyl methacrylates optionally quaternized, acrylate or methacrylate monomers comprising a phosphonate or phosphate group, alkyl imidazolidinone (meth) acrylates, polyethylene glycol (meth) acrylates.
16. An impact modified polymeric article comprising polymeric composition according to claim 1 .