Polymer composition for wire and cable applications with advantageous thermomechanical behaviour and electrical properties

1. An insulation layer comprising a polymer composition, the polymer composition comprising a blend of:

a) a low density polyethylene (LDPE); and

b) a conjugated aromatic polymer;

wherein the LDPE is present in an amount of 90 to 99.99 wt % relative to the total weight of the polymer composition as a whole;

wherein the conjugated aromatic polymer b) is present in an amount of from 0.01 to 10 wt %, relative to the total weight of the polymer composition as a whole;

wherein the insulation layer does not comprise a carbon black,

wherein the polymer composition is prepared by melt-mixing above the melting point of at least the LPDE and the melt-mixed polymer composition is heat treated by remelting at a temperature above the melting temperature of the conjugated aromatic polymer of from 220° C. to 350° C.,

wherein the conductivity of the polymer composition is 1.0 E-12 S/cm or less when measured according to DC conductivity method as described under “Determination Methods”,

wherein DC conductivity when measured according to DC conductivity method as described under “Determination Methods” of the polymer composition is at least 10% lower than an otherwise identical polymer composition not comprising the conjugated aromatic polymer, and

wherein the conjugated aromatic polymer is a polythiophene having the general formula (I):

wherein R 1 is hydrogen and R 2 is hexyl; and

wherein n is an integer in the range 2 to 1000.

2. The insulation layer of claim 1 , wherein the conjugated aromatic polymer b) is present in an amount of 0.02 to 5 wt %, relative to the total weight of the polymer composition as a whole.

3. The insulation layer of claim 1 , wherein the LDPE is selected from a LDPE homopolymer and a LDPE copolymer of ethylene with one or more comonomer(s), wherein the LDPE homopolymer and LDPE copolymer of ethylene with one or more comonomer(s) are optionally unsaturated.

4. The insulation layer of claim 1 , wherein the LDPE is an LDPE homopolymer.

5. The insulation layer of claim 1 , wherein the polymer composition is non crosslinked.

6. The insulation layer of claim 1 , wherein the polymer composition has a strain below 30% after 20 min, when measured in accordance with DMA method A as described under “Determination methods”.

7. A cable comprising one or more conductors surrounded by at least an insulation layer, wherein said insulation layer is as defined in claim 1 .

8. The cable of claim 7 , wherein the cable is a power cable.

9. A process for producing a cable, comprising:

applying on a conductor, at least an insulation layer, wherein the insulation layer is as defined in claim 1 .

10. A method of manufacturing an insulation layer in a cable comprising, using an insulation layer as defined in claim 1 to produce the insulation layer in a cable.