Positive electrode active material for secondary battery, manufacturing method thereof, and secondary battery including same

1. A method for preparing a positive electrode active material for a secondary battery, comprising:

preparing a lithium transition metal oxide including nickel (Ni) and cobalt (Co), and at least one selected from the group consisting of aluminum (Al), manganese (Mn), and a combination thereof;

rinsing the lithium transition metal oxide with water to remove lithium impurities present on a surface of the lithium transition metal oxide; and

subjecting the lithium transition metal oxide rinsed with water to a high-temperature heat treatment to form a high-temperature heat treated lithium transition metal oxide, wherein

the high-temperature heat treatment includes:

elevating a temperature to an elevated temperature;

maintaining the elevated temperature; and

cooling,

wherein an amount of time spent in the elevating the temperature step is 20 to 30% of a total time of the high-temperature heat treatment,

wherein an amount of time spent in the maintaining step is 40 to 50% of the total time of the high-temperature heat treatment, and

wherein an amount of time spent in the cooling step is 20 to 30% of the total time of the high-temperature heat treatment.

2. The method of claim 1 , wherein the total time of the high-temperature heat treatment is 6 to 10 hours.

3. The method of claim 1 , wherein, in the maintaining the elevated temperature step, the elevated temperature step is 600° C. to 900° C.

4. The method of claim 1 , wherein, in the elevating the temperature step, the temperature is elevated at a rate of step 2 to 7° C./min.

5. The method of claim 1 , wherein the cooling step is natural cooling.

6. The method of claim 1 , wherein the high-temperature heat treatment is performed in an oxygen atmosphere having an oxygen partial pressure of 80% or more.

7. The method of claim 1 , wherein the rinsing is performed using 50 to 100 parts by weight of pure water based on 100 parts by weight of the lithium transition metal oxide.

8. The method of claim 1 , wherein the rinsing is performed at a temperature of −10 to 30° C.

9. The method of claim 1 , wherein the lithium transition metal oxide is represented by Formula 1 below:

Li a Ni 1-x1-y1-z1 Co x1 M 1 y1 M 2 z1 M 3 q1 O 2   [Formula 1]

(in Formula 1, M 1 is at least one selected from the group consisting of Mn, Al, and a combination thereof, and M 2 and M 3 are each independently at least one selected from the group consisting of Ba, Ca, Zr, Ti, Mg, Ta, Nb, W, Mo, and a combination thereof, and 1.0≤a≤1.5, 0<x1≤0.2, 0<y1≤0.2, 0≤z1≤0.1, 0<q1≤0.1, and 0<x1+y1+z1≤0.2).

10. The method of claim 1 , wherein the preparing a lithium transition metal oxide is performed by mixing a precursor represented by Formula 2 below and a lithium-containing raw material, and firing the mixture at 700 to 900° C.:

Ni 1-x2-y2-z2 Co x2 M 1 y2 M 2 z2 (OH) 2   [Formula 2]

(in Formula 2, M 1 is at least one selected from the group consisting of Mn, Al, and a combination thereof, M 2 is at least one selected from the group consisting of Ba, Ca, Zr, Ti, Mg, Ta, Nb, W, Mo, and a combination thereof, and 0<x2≤0.2, 0<y2≤0.2, 0≤z2≤0.1, 0≤q2≤0.1, 0<x2+y2+z2≤0.2).

11. The method of claim 1 , wherein the method further comprises:

mixing the high-temperature heat-treated lithium transition metal oxide with at least one selected from the group consisting of H 3 BO 3 , B 2 O 3 , Al 2 O 3 , and a combination thereof to form a mixture, and heat treating the mixture at a temperature of 200 to 500° C. to form a coating layer on the surface of the lithium transition metal oxide.