Catalyst comprising small 10-ring zeolite crystallites and a method for producing hydrocarbons by reaction of oxygenates over said catalyst

1. A catalyst material comprising 10-ring zeolite crystallites with one-dimensional non-intersecting channels, wherein the crystallites have an average length of less than 50 nm, and have a Length/Width ratio of <3.

2. The catalyst material according to claim 1 , having a Si/Al ratio of 15-200.

3. The catalyst material according to claim 1 , wherein the Length/Width ratio is <2.

4. The catalyst material according to claim 1 , wherein the zeolite is ZSM-23.

5. A catalyst comprising a catalyst material comprising 10-ring zeolite crystallites with one-dimensional non-intersecting channels, wherein the crystallites have an average length less than 50 nm, and have a Length/Width ratio of <3.

6. The catalyst according to claim 5 , wherein the 10-ring zeolite crystallites have a Si/Al ratio of 15-200.

7. The catalyst according to claim 5 , wherein the 10-ring zeolite crystallites have a Length/Width ratio below 2.

8. The catalyst according to claim 5 , wherein the zeolite of the 10-ring zeolite crystallites is ZSM-23.

9. A catalyst material comprising 10-ring zeolite crystallites with one-dimensional non-intersecting channels, wherein the crystallites have an average length of less than 150 nm, and have a Length/Width ratio of <2.

10. A method for production of the catalyst material of claim 1 , said method comprising the steps of:

obtaining a gel with a Si/Al ratio of 15-200 by

mixing a silica source and an aluminum source together with a diquaternary ammonium ion SDA in water to form a starting gel,

adjusting the pH by adding a base to the starting gel,

stir the starting gel for times from 0-40 h,

crystallization of the gel by:

heating the gel to a crystallization temperature between 150 to 180° C.,

maintain the crystallization temperature for 6 hours to 60 days,

agitate the gel during crystallization,

recover the crystalline product by filtration and washing until the pH of the filtrate is below pH 8,

dry the filtered and washed product in at least one drying step,

calcine the crystalline product,

ion exchange the calcined product at least once,

calcine the obtained NH4-form of the zeolite to obtain the H-form of the zeolite.

11. The method according to claim 10 , wherein the gel is transferred to an autoclave for crystallization.

12. The method according to claim 10 , wherein the filtered and washed product is dried first at room temperature and then at 100° C. for at least 12 hours.

13. The method according to claim 10 , wherein the ion exchange is carried out with a 1 M solution of NH 4 NO 3 at 60-80° C. for 3-5 h.

14. A process in which an oxygenate is converted to hydrocarbon over a catalyst according to claim 5 ,

wherein the hydrocarbon product comprises less than 5% aromatics,

wherein the hydrocarbon product comprises higher hydrocarbons C5 to C10,

wherein the oxygenate comprises methanol and/or DME,

wherein the process is carried out at a (WHSV) of 1-5 g oxygenate g catalyst −1 h −1 ,

wherein the process is carried out at 1-50 bar,

wherein the process is carried out 350-600° C.

15. A process for producing hydrocarbons, said process comprising the step of reacting an oxygenate stream over the catalyst of claim 5 , thereby producing a hydrocarbon product.

16. The process according to claim 15 , wherein the hydrocarbon product comprises less than 5% aromatics.

17. The process according to claim 15 , wherein the hydrocarbon product comprises higher hydrocarbons C5 to C10.

18. The process according to claim 15 , wherein the oxygenate stream comprises methanol and/or DME.

19. The process according to claim 15 , wherein the process is carried out at a (WHSV) of 1-5 g oxygenate g catalyst −1 h− 1 .

20. The process according to claim 15 , wherein the process is carried out at 1-50 bar.

21. The process according to claim 15 , wherein the process is carried out 350-600° C.