Method for producing an implant comprising calcium carbonate-containing composite powder having microstructured particles having inhibiting calcium carbonate
The invention relates to a method for producing an implant by means of a composite powder having micro structured particles having inhibiting calcium carbonate, wherein the composite powder is obtained by a method in that large polymer particles are joined to small calcium carbonate particles, wherein the calcium carbonate particles are obtained by a method in that calcium carbonate particles are coated with a composition which, in each case based on the total weight thereof, comprises a mixture of at least 0.1 wt % of at least one calcium complexing agent and/or at least one conjugated base which is an alkaline metal or calcium salt of a weak acid, together with at least 0.1 wt % of at least one weak acid.
1. A method for producing an implant comprising a composite powder having microstructured particles having inhibiting calcium carbonate,
wherein initially the composite powder is obtained by bonding large particles to small particles by applying a mechanical load to the composite powder,
wherein the large particles have a mean particle diameter in the range from 0.1 μm to 10 mm,
wherein the large particles comprise at least one polymer,
wherein the small particles are arranged on the surface of the large particles and/or are non-homogeneously spread within the large particles,
wherein the small particles comprise calcium carbonate particles,
wherein the small particles have a mean particle size in the range from 0.01 μm to 1.0 mm,
wherein subsequently the implant is formed by selective laser sintering of a composition comprising the composite powder, and
wherein the small particles are obtained by coating calcium carbonate particles with a composition which, in each case based on its total weight, comprises a mixture of at least 0.1 wt.-% of sodium hexametaphosphate, together with at least 0.1 wt. % of at least one weak acid selected from the group consisting of phosphoric acid, metaphosphoric acid, hexametaphosphoric acid, boric acid, sulfurous acid, and mixtures thereof.
2. The method according to claim 1 , wherein the weak acid is phosphoric acid.
3. The method according to claim 1 , wherein the large particles comprise poly-D, poly-L and/or poly-D,L-lactic acid and/or in that the large particles comprise at least one absorbable polyester having a number average molecular weight in the range from 500 g/mol to 1,000,000 g/mol.
4. The method according to claim 1 , wherein the large particles comprise at least one polyamide and/or in that the large particles comprise at least one polyurethane.
5. The method according to claim 1 , wherein the percentage of the calcium carbonate, based on the total weight of the composite powder, is at least 0.1 wt.-%.
6. The method according to claim 1 , wherein the composite powder, based on the total weight of the composite powder, comprises 40.0 wt.-% to 80.0 wt.-% of PLLA and 20.0 wt.-% to 60.0 wt.-% of calcium carbonate particles.
7. The method according to claim 1 , wherein the content of the sodium hexametaphosphate is within the range from 0.1 parts by weight to 25.0 parts by weight, based on 100 parts by weight of calcium carbonate particles, and the content of the weak acid is within the range from 0.1 parts by weight to 30.0 parts by weight, based on 100 parts by weight of calcium carbonate particles, and/or in that the calcium carbonate has an aspect ratio of less than 5 and/or that the calcium carbonate comprises spherical calcium carbonate and/or in that the large particles comprise at least one thermoplastic polymer and/or in that the large particles comprise at least one absorbable polymer.
8. The method according to claim 7 , wherein the absorbable polymer exhibits inherent viscosity, measured in chloroform at 25° C., 0.1% polymer concentration, in the range from 0.3 dl/g to 8.0 dl/g.
9. A method for producing an implant comprising a composite powder having microstructured particles having inhibiting calcium carbonate,
wherein initially the composite powder is obtained by bonding large particles to small particles by applying a mechanical load to the composite powder,
wherein the large particles comprise at least one polymer,
wherein the small particles are arranged on the surface of the large particles and/or are non-homogeneously spread within the large particles,
wherein the small particles comprise calcium carbonate particles,
wherein subsequently the implant is formed by selective laser sintering of a composition comprising the composite powder, and
wherein the small particles are obtained by coating calcium carbonate particles with a composition which, in each case based on its total weight, comprises a mixture of at least 0.1 wt.-% of sodium hexametaphosphate, together with at least 0.1 wt. % of at least one weak acid selected from the group consisting of phosphoric acid, metaphosphoric acid, hexametaphosphoric acid, boric acid, sulfurous acid, and mixtures thereof.
10. A method for producing an implant comprising a composite powder having microstructured particles having inhibiting calcium carbonate,
wherein initially the composite powder is obtained by bonding large particles to small particles by applying a mechanical load to the composite powder,
wherein the small particles are arranged on the surface of the large particles and/or are non-homogeneously spread within the large particles,
wherein subsequently the implant is formed by selective laser sintering of a composition comprising the composite powder, and
wherein the small particles are obtained by coating calcium carbonate particles with a composition which, in each case based on its total weight, comprises a mixture of at least 0.1 wt.-% of sodium hexametaphosphate, together with at least 0.1 wt. % of at least one weak acid selected from the group consisting of phosphoric acid, metaphosphoric acid, hexametaphosphoric acid, boric acid, sulfurous acid, and mixtures thereof.