Optical film having organic and inorganic particles of different sizes, and polarizing plate comprising same
The present invention relates to a resin composition for forming an optical film, an optical film, and a polarizing plate, in which the resin composition for forming an optical film improves adhesion between an antiglare layer and a light-transmitting substrate film and enables the antiglare layer and the optical film to exhibit excellent optical properties such as appropriate haze, low gloss value, and excellent antiglare properties. The composition for forming an optical film is a resin composition for forming an optical film for forming an infiltration layer and an antiglare layer having surface irregularities on a light-transmitting substrate film, and comprises: a binder-forming compound including a polyfunctional (meth)acrylate-based compound having three or more functionalities, and a permeable compound having a hydrophilic functional group and a photo-curable functional group; two or more light-transmitting fine particles having a sub-micron (sub-μm) scale; and a permeable solvent capable of dissolving at least a part of the light-transmitting substrate film, wherein the binder-forming compound and the permeable solvent have a weight ratio of 1:0.04 or more.
1. An optical film comprising:
a light-transmitting substrate film;
an infiltration layer having at least a part that is infiltrated into the light-transmitting substrate film so as to overlap with at least a part of the light-transmitting substrate film, and including a first binder containing a first (meth)acrylate-based cross-linked polymer; and
an antiglare layer which includes a second binder containing a second (meth)acrylate-based cross-linked polymer, and at least two light-transmitting fine particles dispersed on the second binder, and is formed so as to have surface irregularities on the infiltration layer, wherein the at least two light-transmitting fine particles comprise organic fine particles having a particle diameter of 1 to 5 μm and inorganic fine particles having a particle diameter of 10 nm to 300 nm,
wherein the infiltration layer has a thickness of 600 nm or more and 1.0 μm or less,
wherein the antiglare layer has a thickness of 4.4 to 10 μm, and
wherein the optical film has a total haze value of 1 to 5% and a 60-degree gloss value of 80% to 88%.
2. The optical film of claim 1 , wherein the optical film has a 20-degree gloss value of 45% to 68%.
3. The optical film of claim 1 , wherein the second binder has a refractive index of 1.50 to 1.60.
4. The optical film of claim 1 , further comprising a low refractive index layer which is formed on the antiglare layer and includes a binder resin containing a (co)polymer of a photopolymerizable compound and hollow silica particles dispersed in the binder resin.
5. The optical film of claim 4 , wherein the low refractive index layer has a refractive index of 1.3 to 1.5 and a thickness of 1 to 300 nm.
6. A polarizing plate comprising the optical film of claim 1 .