Method for producing pellets, method for producing resin molded article, and pellets
Provided are a method for producing pellets that are easy to be uniformly molded at the time of using the pellet for molding even when the pellets include a large amount of inorganic substance particles, the pellets, and a method for molding a resin molded article. The method for producing pellets according to the present invention includes a method for producing pellets formed from a resin composition including a crystalline macromolecule and an inorganic fine powder or organic fine powder in a mass ratio of 50:50 to 20:80, the method including the step of kneading the crystalline macromolecule and the inorganic fine powder or the organic fine powder so that the microcrystalline size of the crystalline macromolecule is 190 Å or smaller. The pellets according to the present invention are pellets formed from a resin composition including a crystalline macromolecule having a microcrystalline size of 190 Å or smaller, and inorganic substance particles in a mass ratio of 50:50 to 20:80.
1. A method for producing pellets formed from a resin composition including a crystalline macromolecule and an inorganic fine powder in a mass ratio of 50:50 to 20:80, the method comprising the step of:
kneading the crystalline macromolecule and the inorganic fine powder at a temperature that is at least 45° C. higher than a melting point of the crystalline macromolecule so that the crystalline macromolecule has a microcrystalline size of 190 Å or smaller,
wherein an average particle diameter of the inorganic fine powder is 50 μm or smaller.
2. The method according to claim 1 , wherein the crystalline macromolecule includes a polypropylene resin or a polyethylene resin.
3. The method according to claim 1 , wherein the inorganic fine powder includes calcium carbonate particles.
4. The method according to claim 1 , wherein the pellets are molded by the kneading at the temperature equal to or higher than a temperature at which the microcrystalline size of the crystalline macromolecule is 190 Å or smaller.
5. A method for producing a resin molded article, the method comprising steps of:
producing the pellets by the method for producing pellets according to claim 1 ; and
molding the pellets into the resin molded article.