Preparation and applications of 3D bioprinting bioinks for repair of bone defects, based on cellulose nanofibrils hydrogels with natural or synthetic calcium phosphate particles
The present invention relates to preparation of bioink composed of cellulose nanofibril hydrogel with native or synthetic Calcium containing particles. The concentration of the calcium containing particles can be between 1% and 40% w/v. Such bioink can be 3D Bioprinted with or without human or animal cells. Coaxial needle can be used where cellulose nanofibril hydrogel filled with Calcium particles can be used as shell and another hydrogel based bioink mixed with cells can be used as core or opposite. Such 3D Bioprinted constructs exhibit high porosity due to shear thinning properties of cellulose nanofibrils which provides excellent printing fidelity. They also have excellent mechanical properties and are easily handled as large constructs for patient-specific bone cavities which need to be repaired. The porosity promotes vascularization which is crucial for oxygen and nutrient supply. The porosity also makes it possible for further recruitment of cells which accelerate bone healing process. Calcium containing particles can be isolated from autologous bone, allogenic bone or xenogeneic bone but can be also isolated from minerals or be prepared by synthesis. Preferable Calcium containing particles consist of β-tricalcium phosphate which is resorbable or natural bone powder, preferably of human or porcine origin. The particles described in the present invention have particle size smaller than 400 microns, or more preferably smaller than 200 microns, to make it possible to handle in printing nozzle without clogging and to obtain a good resolution. Cellulose nanofibrils can be produced by bacteria orbe isolated from plants. They can be neutral, charged or oxidized to be biodegradable. The bioink can be additionally supplemented by other biopolymers which provide crosslinking. Such biopolymers can be alginates, chitosans, modified hyaluronic acid or modified collagen derived biopolymers.
1. A bioink for use in 3D bioprinting, wherein the bioink is suitable for use with living cells and consists essentially of a cellulose nanofibril based hydrogel; a biopolymer selected from the group consisting of: alginates, hyaluronic acid, agarose, chitosan, fibrin, collagen, and gelatin; and 1-40% (w/v) calcium-containing particles, wherein the calcium-containing particles have a fraction size smaller than 400 microns and consist essentially of β-tricalcium phosphate, biphasic HA-TCP, or natural bone powder.
2. The bioink according to claim 1 , wherein said calcium-containing particles have a fraction size smaller than 200 microns.
3. The bioink according to claim 1 , wherein the natural bone powder is of human or porcine origin.
4. The bioink according to claim 1 , wherein the cellulose nanofibril is provided by one of the following alternatives: biosynthetization by bacteria, isolation from wood, isolation from primary cell wall or isolation from tunicates.
5. A cellular bioink composition comprising the bioink of claim 1 and living cells.
6. The cellular bioink composition according to claim 5 , wherein the living cells are mesenchymal stem cells, osteoblasts, or induced pluripotent stem cells (iPSC).
7. A method for preparing a 3D bioprinting construct that is suitable for use in implants to repair dental defects or bone defects in a human or animal body comprising:
a) providing a bioink according to claim 1 , and
b) printing a construct with the bioink and a bioprinter apparatus.
8. A method for preparing a 3D bioprinting construct that is suitable for use in implants to repair dental defects or bone defects in a human body or animal body comprising:
a) providing a bioink of claim 1 ,
b) providing living cells,
c) mixing the components from a) and b) to obtain a cellular bioink composition,
d) printing a construct with the cellular bioink composition of c) and a bioprinter apparatus, and
e) optionally incubating the construct of d) in an environment suitable for cells in the construct to differentiate.
9. A 3D bioprinted construct prepared by the method according to claim 8 .
10. The 3D bioprinted construct of claim 9 , wherein a coaxial needle is further used in the bioprinter apparatus for printing the construct, and wherein the construct comprises a core and a shell, wherein
(i) the core comprises the bioink of a) and the shell comprises the cellular bioink composition of d); or
(ii) the core comprises the cellular bioink composition of d) and the shell comprises the bioink of a).
11. The 3D bioprinted construct of claim 9 , wherein the living cells are mesenchymal stem cells that are differentiated into osteoblasts in the constructs, or wherein the living cells are osteoblasts or induced pluripotent stem cells (iPSC).
12. The 3D bioprinted construct according to claim 9 , wherein the construct is an implant suitable to repair dental defects or bone defects in a human or animal body.
13. The 3D bioprinted construct according to claim 9 , wherein the construct is suitable for use in drug discovery or as a disease model.
14. A method for repairing a bone defect in a human or animal body, comprising implanting in the body in need thereof the construct of claim 12 , wherein living bone tissue is created.
15. A 3D bioprinted living bone tissue prepared by the method according to claim 14 .
16. The 3D bioprinted living bone tissue according to claim 15 , wherein the tissue comprises living osteoblasts and wherein spaces between bioink printed grids allow diffusion of nutrients, oxygen, proteins and/or growth factors.
17. The 3D bioprinted living bone tissue according to claim 15 , wherein the living cells are osteoblasts that are cultured to build bone.
18. A method for treatment of an animal or human patient suffering from a tissue defect, lack of tissue or need for replacement of a tissue, comprising implanting in the tissue of the patient the bioprinted living tissue of claim 15 .
19. The method for treatment according to claim 18 , wherein the tissue is chosen from bone or tooth.
20. A method for repairing a dental defect in a human or animal body, comprising implanting into the body in need thereof a construct prepared by the method of claim 7 .
21. The bioink according to claim 1 , wherein the cellulose nanofibril and alginate are in a concentration of 2-3% based on the dry weight of the bioink.