CONFORMABLE POLYETHYLENE FABRIC AND ARTICLES MADE THEREFROM
A fabric comprises a highly drawn UHMWPE non-filamentary sheet having a width of at least 10 mm and a plurality of impalements wherein one impalement is separated from the next impalement by a distance of at least 1 mm. The fabric may further comprise a plurality of said sheets wherein each sheet is stacked one on top of the other.
1 . A fabric comprising a highly drawn UHMWPE non-filamentary sheet having a width of at least 10 mm and a plurality of impalements wherein each impalement is separated from each other impalement by a distance of at least 1 mm and wherein the fabric has a mean speed of sound above 2500 m/s.
2 . The fabric of claim 1 , wherein the plurality of impalements in the fabric are slits, holes or filaments passing through the plane of the UHMWPE non-filamentary sheet.
3 . The fabric of claim 1 , wherein each impalement is separated from each other impalement by a distance of at least 2 mm.
4 . The fabric of claim 1 , further comprising a non-UHMWPE polymeric film, a nonwoven sheet, a woven sheet or an adhesive adjacent to the UHMWPE non-filamentary sheet.
5 . The fabric of claim 1 , wherein the UHMWPE non-filamentary sheet has a tenacity of at least 15 gpd (1.3 N/tex).
6 . The fabric of claim 1 , wherein the plurality of impalements are arranged in rows.
7 . The fabric of claim 1 , wherein the plurality of impalements are in a random arrangement.
8 . The fabric of claim 2 , wherein the filaments passing through the plane of the UHMWPE non-filamentary sheet do so at an angle of from 70 to 90 degrees with respect to the plane of the UHMWPE non-filamentary sheet.
9 . The fabric of claim 6 , wherein the impalements in one row are offset with respect to the impalements in the next row.
10 . A fabric comprising a plurality of UHMWPE non-filamentary sheets of claim 1 , wherein each UHMWPE non-filamentary sheet is stacked one on top of the other.
11 . The fabric of claim 10 , wherein each UHMWPE non-filamentary sheet in the stack is placed in an orientation such that the direction of draw in one UHMWPE non-filamentary sheet is offset with respect to the direction of draw in the next UHMWPE non-filamentary sheet.
12 . The fabric of claim 10 , further comprising filaments passing through the plane of the stack of UHMWPE non-filamentary sheets.
13 . The fabric of claim 10 , further comprising a non-UHMWPE polymeric sheet, nonwoven sheet, a woven sheet or an adhesive adjacent to the UHMWPE non-filamentary sheets.
14 . The fabric of claim 10 , wherein each UHMWPE non-filamentary sheet in the stack is placed in an orientation such that the direction of draw in one UHMWPE non-filamentary sheet is orthogonal with respect to the direction of draw in the next UHMWPE non-filamentary sheet.
15 . The fabric of claim 12 , wherein the filaments passing through the plane of the UHMWPE non-filamentary sheet do so at an angle of from 70 to 90 degrees with respect to the plane of the UHMWPE non-filamentary sheet.
16 . An article comprising a fabric of claim 1 .
17 . (canceled)
18 . The article of claim 16 , wherein the article is ballistic-resistant and has a kinetic energy absorption per areal density against 1.04 gram, 5.56 mm diameter, right circular steel cylinders impacting end of 15 J m 2 /kg or higher.
19 . The article of claim 16 , wherein the article is cut-resistant and has a Cut Resistance Performance Level of A2 or greater, as determined by the analysis defined in ANSI/ISEA 105-2016 from cut resistance data generated via test method ASTM F2992/F2992M-15.
20 . An article comprising a fabric of claim 10 , wherein at least 50% of the plurality of impalements do not rupture the highly drawn UHMWPE non-filamentary sheets perpendicular to their orientation directions.
21 . The fabric of claim 1 , wherein at least 10% of the plurality of impalements do not penetrate fully through the fabric.